Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Ultra high cycle fatigue behavior of a medium-carbon high strength spring steel NHS1

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Very High Cycle Fatigue Behaviour of 2000‐mpa Ultra‐high‐strength Spring Steel with Bainite–martensite Duplex Microstructure

Ultra High Cycle Fatigue Behavior of Automotive High Strength Spring Steels 54sicrv6 and 54Sicr6

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

High-Cycle Fatigue Fracture Behavior of Ultrahigh Strength Steels

Fatigue fracture behaviour of a medium-carbon 2 000 MPa level high strength spring steel

Gigacycle Fatigue Behavior of 1800 MPa Grade High Strength Spring Steel for Automobile Lightweight

Effect of Inclusion Size on High-Cycle Fatigue Behavior of High Strength Spring Steel

On the Formation of GBF of High-Strength Steels in the Very High Cycle Fatigue Regime

GIGACYCLE FATIGUE OF ULTRA-HIGH STRENGTH STEELS

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

Comparative Study of High-Cycle Fatigue and Failure Mechanisms in Ultrahigh-Strength CrNiMoWMnV Low-Alloy Steels

Influence of Inclusion Size on Fatigue Behavior of High Strength Steels in the Gigacycle Fatigue Regime

Influence of Non-Metallic Inclusions on Very High-Cycle Fatigue Performance of High-Strength Steels and Interpretation via Crystal Plasticity Finite Element Method

High-Cycle, Low-Cycle, Extremely Low-Cycle Fatigue and Monotonic Fracture Behaviors of Low-Carbon Steel and Its Welded Joint

Failure Behavior of Ultra-high Cycle Fatigue of a 2 000 MPa Grade High Strength Steel