Abstract:Employed as thermal protection coating for engine blades,thermal barrier coatings(TBCs) can significantly increase service life of these components in a high-temperature environment.A systematic investigation on the properties of interface between TBCs and nickel based superalloy substrate was carried out.The elasticity modulus of ceramic layer,the hardness of ceramic coat and the microstructure change near the ceramic layer-adhesive layer interface before and after isothermal heat treatment were experimentally obtained and compared.Results show that during isothermal heat treatment,the ceramic coat sintering has occurred but there is not phase transformation;besides,both Young's modulus and the hardness increase first then decrease along with the heat treatment time increasing;the thickness of oxide layer grows along with the heat treatment time and temperature increasing.Moreover,by using multi-phase angle interfacial fracture toughness test method proposed in this paper,a failure criterion for TBCs interface was established in terms of stress intensity factors as characterization parameters.Assuming the interfaces is viscous contact,the evolution of interface carrying capacity along with the increasing of ceramic coat Young's modulus and oxide layer thickness was predicted.Thermal fatigue properties and failure mechanism of interface between TBCs and nickel based superalloy substrate were investigated by thermal cycling test.Results reveal that along with the increase of thermal cycle temperature holding time,the fatigue life increases first then decreases,and the failure mode translates from single interface failure into both interface failure and ceramic failure.

Study on Thermal Fatigue Life Prediction for Plasma Sprayed Thermal Barrier Coatings on the Surface of Turbine Vane

Thermal Fatigue of Atmospheric Plasma Sprayed Thermal Barrier Coatings

Thermal Fatigue Life Prediction of Thermal Barrier Coat on Nozzle Guide Vane Via Master–Slave Model

Failure Characteristics and Life Prediction for Thermally Cycled Thermal Barrier Coatings

Simulation of Residual Stresses and Their Effects on Thermal Barrier Coating Systems Using Finite Element Method

Prediction of thermal fatigue life of a turbine nozzle guide vane

Experimental Investigation on High-Temperature Fatigue and Fracture Properties at the Interface Between Thermal Barrier Coatings (tbcs) and Nickel Based Superalloy Substrate

Numerical Assessment of Thermal Insulation and Stress Responses in Film-Cooled Turbine Vane Thermal Barrier Coatings under CMAS Deposition Conditions

Deformation Prediction Theory of Thermal Barrier Coatings near Cooling Holes under Thermal Cycling

Thermomechanical and Thermal Gradient Mechanical Fatigue Lifetime of Thermal Barrier Coating Systems

Analysis On Stress Distribution Of Thermal Barrier Coating System With Thermal Gradient Mechanical Fatigue

Rapidity dependence of the photon to pion production ratio in high energy collisions

Prediction of long-term fatigue life of CFRP composite hydrogen storage vessel based on micromechanics of failure

Chemo-thermo-mechanical modeling of EB-PVD TBC failure subjected to isothermal and cyclic thermal exposures

Numerical and Experimental Investigation of Residual Stress in Thermal Barrier Coatings During Aps Process

Research on the contact fatigue failure of thermal sprayed coating based on infrared thermography

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient

Thermal-Fluid-Solid Coupling Analysis on the Temperature and Thermal Stress Field of a Nickel-Base Superalloy Turbine Blade

Failure prediction of thermal barrier coatings on turbine blades under calcium-magnesium-alumina-silicate corrosion and thermal shock

Fracture Behavior of TBCs with Cooling Hole Structure under Cyclic Thermal Loadings

RESEARCH PROGRESS ON THE EXPERIMENTAL MEASUREMENT METHODS OF MECHANICAL PROPERTIES OF THERMAL BARRIER COATINGS