Abstract:Thermal barrier coatings (TBCs) material has excellent high-temperature resistance and heat insulation performance, which plays a vital role in improving the working efficiency and running life of the engine. During the flight, the engine will inhale dust particles in the air. These particles are mostly from siliceous debris, which are usually called calcium magnesium aluminum silicate (CMAS). At present, CMAS corrosion has become one of the important problems affecting the service life of thermal barrier coatings. In this study, conventional yttrium oxide stabilized zirconia (YSZ) coatings and ytterbium oxide and yttrium oxide co-stabilized zirconia (YbYSZ) coatings were prepared by atmospheric plasma spraying. The two coatings were examined under thermal cycling-CMAS coupling conditions and divided into six life stages. The failure modes, CMAS permeation behavior, crack characteristics and mechanical properties of the two coatings at different life stages were evaluated systematically. The experimental results show that the YbYSZ coating has a longer life than YSZ coating under the thermal cycling and CMAS coupling condition, which increases by about 83% compared with the conventional YSZ coating. In the whole life stage, the porosity of YbYSZ coating is always higher than that of YSZ coating. The phase transition is not the reason for the failure and spalling of the coatings. The crack length of the two coatings showed an increasing trend, but the crack length of the YSZ coating was higher than that of the YbYSZ coating, and the crack density of the two coatings showed a "saddle shape", which was more obvious for the YSZ coating. The YbYSZ coating shows better mechanical properties under the thermal cycling-CMAS coupling condition with the evolution of life.

Failure prediction of thermal barrier coatings on turbine blades under calcium-magnesium-alumina-silicate corrosion and thermal shock

Failure behavior study of EB-PVD TBCs under CMAS Corrosion and Thermal Shock Cycles

Deformation Prediction Theory of Thermal Barrier Coatings near Cooling Holes under Thermal Cycling

Prediction of Microstructure and Mechanical Properties of Atmospheric Plasma-Sprayed 8YSZ Thermal Barrier Coatings Using Hybrid Machine Learning Approaches

Rapidity dependence of the photon to pion production ratio in high energy collisions

Failure Behavior Study of EB-PVD TBCs under Salt Spray Corrosion and Thermal Shock Cycles

Performance and Failure Modes of Thermal Barrier Coatings Deposited by EB-PVD on Blades under Real Service Conditions in Gas Turbine

Nondestructive Evaluation of Thermal Barrier Coatings Thickness Using Terahertz Time-Domain Spectroscopy Combined with Hybrid Machine Learning Approaches

Failure Mechanism of EB-PVD Thermal Barrier Coatings under the Synergistic Effect of Thermal Shock and CMAS Corrosion

Prediction of Fatigue Crack Damage Using In-Situ Scanning Electron Microscopy and Machine Learning

Simulation of Residual Stresses and Their Effects on Thermal Barrier Coating Systems Using Finite Element Method

Multiscale Prediction of Thermal Damage for Hybrid Fibers Reinforced Cementitious Composites Blended with Fly Ash at High Temperatures

Research on Modified Thermal Barrier Coatings Against CMAS Corrosion Driven by Mechanism–Data Hybrid Model

Numerical Assessment of Thermal Insulation and Stress Responses in Film-Cooled Turbine Vane Thermal Barrier Coatings under CMAS Deposition Conditions

Failure Characteristics and Life Prediction for Thermally Cycled Thermal Barrier Coatings

Deep Learning-Based Modeling Method for Probabilistic LCF Life Prediction of Turbine Blisk

Thermal Barrier Coatings in burner rig experiment analyzed through LAser Shock for DAmage Monitoring (LASDAM) method

Damage Grading Evaluation of Thermal Barrier Coatings under CMAS Corrosion

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient

Chemo-thermo-mechanical modeling of EB-PVD TBC failure subjected to isothermal and cyclic thermal exposures