Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Fabrication and Characterization for Transparent Electrodes of Tio2 Nanotube Arrays on Fluorine-Doped Tin Oxide-Coated Glass

Synthesis and characterization of TiO 2 nanotube film on fluorine-doped tin oxide glass

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Fabrication and Photoelectrochemical Properties of Highly Ordered TiO_2 Nanotube Arrays on Glass Substrate

(Invited) Fabrication of High-Quality TiO2 Nanotubes on Conductive Glasses

Photoelectrochemical Properties of Ag/TiO2 Electrodes Constructed Using Vertically Oriented Two-Dimensional TiO2 Nanosheet Array Films

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

High-quality Self-Ordered TiO 2 Nanotubes on Fluorine-Doped Tin Oxide Glass

Fabrication of Titanium dioxide nanotube photo-electrodes in different electrolyte mixtures and the impacts on their characteristics and photo-catalytic abilities under visible light

Transferable TiO2 Nanotubes Membranes Formed Via Anodization and Their Application in Transparent Electrochromism

Facile Fabrication, Characterization, and Enhanced Photoelectrocatalytic Degradation Performance of Highly Oriented Tio2 Nanotube Arrays

Fabrication and formation mechanism of self-organized TiO2 nanotube arrays

Preparation and Photoelectrocatalytic Performance of TiO<sub>2</sub> Nano-Tubes Arrays Electrode

Characterization of TiO 2 Nanotube Arrays Prepared Via Anodization of Titanium Films Deposited by DC Magnetron Sputtering

Preparation and Photoelectrocatalytic Performance of TiO2 Nano-Tubes Arrays Electrode

Fabrication of TiO2 Nanotube by Electrochemical Anodization: Toward Photocatalytic Application

Deposition of transparent TiO 2 nanotubes-films via electrophoretic technique for photovoltaic applications

Photoelectrochemical performance of TiO2 photoanodes: Nanotube versus nanoflake electrodes

Fluoride concentration controlled TiO2 nanotubes: the interplay of microstructure and photocatalytic performance

Synthesis and Photoelectrochemical Properties of Self-Organized Anodic TiO2 Nanotube Arrays

Fabrication of TiO2 Nanotube Arrays by Electrochemical Anodization in an NH4F/H3PO4 Electrolyte