Abstract:A novel technique, the pulsed-laser-induced liquid-deposition (PLLD) method, has been employed to grow nanocrystalline TiO2 films on fluorine-doped tin-oxide-coated (FTO) glass substrates at room temperature. The PLLD method was implemented by directing a pulsed laser into a liquid precursor and depositing the photosynthesized nanocrystalline TiO2 on an FTO glass substrate immersed in the liquid precursor. The as-grown nanocrystalline TiO2 films were found to have a rutile crystal structure and consist of a number of flower-like TiO2 crystal units arrayed together on the FTO glass substrate. Each of the flower-like TiO2 crystal units was composed of many nanostructured TiO2 whiskers, and their building blocks were found to be bundles of TiO2 nanorods with diameter of about 5 nm. The growth of these TiO2 nanorods is highly anisotropic, with the preferential growth direction along [001]. As-grown nanocrystalline TiO2 films were annealed at 450°C in air for 30 min for the applications of dye-sensitized solar cells, and the nanostructured characteristics with good porosity were preserved after annealing. A preliminary dye-sensitized solar cell was built based on the annealed nanocrystalline TiO2 film. The results suggest that the PLLD method is a promising technique for growing nanocrystalline TiO2 films for photovoltaic applications.

High-quality Self-Ordered TiO 2 Nanotubes on Fluorine-Doped Tin Oxide Glass

(Invited) Fabrication of High-Quality TiO2 Nanotubes on Conductive Glasses

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Synthesis and characterization of TiO 2 nanotube film on fluorine-doped tin oxide glass

Synthesis of Highly-Ordered Tio2 Nanotube Arrays with Tunable Sizes

Large-scale, noncurling, and free-standing crystallized TiO2 nanotube arrays for dye-sensitized solar cells

Effect of Acid Solution, Fluoride Ions, Anodic Potential and Time on the Microstructure and Electronic Properties of Self-Ordered TiO 2 Nanotube Arrays

Characterization of TiO 2 Nanotube Arrays Prepared Via Anodization of Titanium Films Deposited by DC Magnetron Sputtering

Fast Growth of Highly Ordered TiO2 Nanotube Arrays on Si Substrate under High-Field Anodization

The Large Diameter and Fast Growth of Self-Organized TiO2 Nanotube Arrays Achieved Via Electrochemical Anodization.

Growth of Nanocrystalline Tio2 Films by Pulsed-Laser-Induced Liquid-Deposition Method and Preliminary Applications for Dye-Sensitized Solar Cells

Anodization Fabrication of Highly Ordered Tio2 Nanotubes

Fabrication and formation mechanism of self-organized TiO2 nanotube arrays

Characteristics and Electronic Properties of Self-Organized Tio2 Nanotube Arrays Fabricated on Ti Foil by Square Wave Pulse Anodizing Ti in an Hf + H2so4 Solution

Fabrication and Photoelectrochemical Properties of Highly Ordered TiO_2 Nanotube Arrays on Glass Substrate

Controlling anodization time to monitor film thickness, phase composition and crystal orientation during anodic growth of TiO2 nanotubes

Facile Fabrication of Open-Ended TiO2 Nanotube Arrays with Large Area for Efficient Dye-Sensitized Solar Cells

Free-standing TiO(2) nanotube arrays made by anodic oxidation and ultrasonic splitting.

Review of Water-Assisted Crystallization for TiO 2 Nanotubes

Low-Temperature Synthesis of High-Ordered Anatase Tio2 Nanotube Array Films Coated with Exposed {001} Nanofacets

Review of Water-Assisted Crystallization for TiO2 Nanotubes