Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Synthesis and Photoelectrochemical Properties of Self-Organized Anodic TiO2 Nanotube Arrays

Synthesis and Photoelectrochemical Properties of Self-Organized Anodic TiO<sub>2</sub> Nanotube Arrays

Photoelectrochemical Properties of Ag/TiO2 Electrodes Constructed Using Vertically Oriented Two-Dimensional TiO2 Nanosheet Array Films

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Temperature-dependent differences in wettability and photocatalysis of TiO 2 nanotube arrays thin films

Silver-Decorated Tio2 Nanorod Array Films with Enhanced Photoelectrochemical and Photocatalytic Properties

Fabrication and formation mechanism of self-organized TiO2 nanotube arrays

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

Highly Ordered TiO2 Nanotube Arrays with Engineered Electrochemical Energy Storage Performances

Fabrication and Field Emission Characteristics of TiO2 Nano-Tube Arrays

Synthesis of TiO<sub>2</sub> Nanotube Arrays Through Multistep Anodization

Controllable Synthesis of Well-Ordered TiO2 Nanotubes in a Mixed Organic Electrolyte for High-Efficiency Photocatalysis

Synthesis And Photovoltaic Application Of High Aspect-Ratio Tio2 Nanotube Arrays By Anodization

TiO2 nanotube arrays prepared by anodic oxidation method

Preparation of TiO2 Nanotube Photocatalyst by Anodization and Improvement of Photocatalytic Performance

TiO<sub>2</sub> Nanowires/Nanobelts Originating from Anodically Grown Nanotube Arrays

Electron Field Emission and Photoluminescence of Anatase Nanotube Arrays

Synthesis of Highly-Ordered Tio2 Nanotube Arrays with Tunable Sizes

Fabrication of TiO2 Nanotube by Electrochemical Anodization: Toward Photocatalytic Application

Enhanced Photoelectrochemical Properties of Ta-TiO2 Nanotube Arrays Prepared by Magnetron Sputtering

Electrochemical Method for Synthesis of a ZnFe2O4/TiO2 Composite Nanotube Array Modified Electrode with Enhanced Photoelectrochemical Activity