Abstract:A composite titania thin film consisted of quasi-aligned single-crystalline rutile nanorods embedded in sol-gel-derived anatase aggregates was fabricated and its photoelectrochemical behavior was studied in detail. A monolayer of nearly sing I e-crystal line rutile nanorods was first deposited on metallic Ti substrates through a controlled reaction between Ti and hydrogen peroxide. The gaps among the rutile nanorods were then filled with titania nanoparticles through a sol-gel dip-coating approach, which achieved a composite thin film of single-crystalline rutile nanorods embedded in anatase aggregates, after a subsequent thermal treatment at 723 K. The X-ray diffraction measurement revealed that the composite film with thickness of 180 nm contained anatase and rutile in a nearly 50:50 ratio. The UV-visible diffusive reflectance spectra estimated a band gap of 2.99 eV for the rutile monolayer and a slightly increased value of 3.03 eV for the composite film due to the embedding of the anatase nanoparticles. Photocurrent versus potential diagrams, photocurrent transient curves, and open-circuit potential measurement supported the fact that the anatase nanoparticles possessed better inherent photoelectrochemical properties than rutile. However, electrochemical impedance spectra characterization, together with photocurrent transient curves and open-circuit potential measurement, suggests that the single-crystalline rutile nanorods exhibited a higher electron-transfer rate. The combination of the two components in such an appropriate way enhanced significantly the charge separation effect arising from the anatase/rutile couple, which hence combined efficiently the "mixed crystal effect" and the "mixed morphological effect". A steady-state photocurrent more than double the simple sum of those generated by the two components alone was detected for the current composite film, which can be attributed to the single-crystalline rutile nanorods that provide channels for rapid electron transfer to the conductive Ti substrates under an applied bias potential. As a result, this study concludes that the present nanostructure magnified significantly the well-established mixed crystal effect, that is, an enhanced charge separation arising from a mixture of anatase and rutile.

Photoelectrochemical performance of TiO2 photoanodes: Nanotube versus nanoflake electrodes

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Photoelectrochemical Properties of Ag/TiO2 Electrodes Constructed Using Vertically Oriented Two-Dimensional TiO2 Nanosheet Array Films

Electrodeposited Cu2O on the {101} Facets of TiO2 Nanosheet Arrays and Their Enhanced Photoelectrochemical Performance

Photocurrent conversion efficiency of TiO2 nanotube photoanodes in dependence of illumination intensity

Enhanced Photoelectrochemical Response of a Composite Titania Thin Film with Single-Crystalline Rutile Nanorods Embedded in Anatase Aggregates

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

Femtosecond laser mediated fabrication of micro/nanostructured TiO2- photoelectrodes: Hierarchical nanotubes array with oxygen vacancies and their photocatalysis properties

A novel approach to titania nanowire arrays as photoanodes of back-illuminated dye-sensitized solar cells

Highly Enhanced Photoelectrocatalytic Properties by Α-Fe 2 O 3 Modified NF-TiO 2 Pyramids with Dominant (101) Facets

Photoelectrocatalytic Efficiency of Low-Temperature Precipitated Monolayer Rutile TiO 2 Nanoflower Film

Explaining the Enhanced Photoelectrochemical Behavior of Highly Ordered TiO2 Nanotube Arrays: Anatase/Rutile Phase Junction

Synthesis of Co3O4/Ag/TiO2 Nanotubes Arrays Via Photo-Deposition of Ag and Modification of Co3O4 (311) for Enhancement of Visible-Light Photoelectrochemical Performance

Enhanced Photoelectrochemical Property of TiO 2 Nanotube Array Photoanode Deposited with Al,Cr-Codoped SrTiO 3 Nanocubes

Synthesis and Photoinduced Charge-Transfer Properties of a ZnFe2O4-sensitized TiO2 Nanotube Array Electrode.

Photoelectrochemical properties of TiO2 coated on carbon nanofibers with different microstructure film electrodes

Comparative Analysis of Anodized TiO2 Nanotubes and Hydrothermally Synthesized TiO2 Nanotubes: Morphological, Structural, and Photoelectrochemical Properties

Investigation on the Photoelectrocatalytic Activity of Well-Aligned Tio2 Nanotube Arrays

Electrochemical Method for Synthesis of a ZnFe2O4/TiO2 Composite Nanotube Array Modified Electrode with Enhanced Photoelectrochemical Activity

Different crystalline phases of aligned TiO2 nanotubes and their UV photoelectric properties

Photoelectrochemical Properties of TiO2/SrTiO3 Combined Nanotube Arrays