Abstract:The rheological properties of fresh cement pastes (FCPs) in the presence of superplasticizer were systematically investigated in this study where influential factors such as mix proportion including the water-to-cement (W/C) ratio and superplasticizer-to-cement (Sp/C) ratio, temperature, and time were discussed. The initial yield stress of FCPs with varied mix proportions and its development over time were tested at 0, 20, and 40 degrees C to characterize the rheological properties of the pastes. Measurements on the amount of adsorbed superplasticizer, zeta potential, particle size, microscopic observation, and calorimetry were performed to quantify the influences of superplasticizer on the microstructure of FCPs under varied mix proportions and temperatures. Results indicate that the initial yield stress of the pastes and its development over time evidently descend due to the plasticizing effect and retardation effect of superplasticizer. Higher temperature facilitates a sharper rise in the initial yield stress and the growth of yield stress with time while the effects of temperature are weakened in the case of high W/C ratio or Sp/C ratio. Higher temperature results in a larger adsorbed amount and a higher zeta potential, which is believed to result from the accelerated dissolution and hydration rate. The effects of W/C ratio, superplasticizer dosage, and temperature on the development of yield stress over time were integrated into the parameter of relative hydration degree. A generalized model to describe the evolution of yield stress was deduced by introducing the hydration index of relative hydration degree , which was verified by the experimental results that the yield stress ascended in a roughly linear fashion with 1/(1-).

Interaction Between Superplasticizer and Cement by Electrical Resistivity Method

Influence of Superplasticizers on Early Age Drying Shrinkage of Cement Paste with the Same Consistency

Influence of Superplasticizer Type and Dosage on Early-age Drying Shrinkage of Cement Paste with Consideration of Pore Size Distribution and Water Loss

The Early-Age Drying Shrinkage of Cement-Based Materials with the Same Workability after Temperature Compensation

Rheological properties and microstructure of fresh cement pastes with varied dispersion media and superplasticizers

The Adsorption Behavior of PNS Superplasticizer and Its Relation to Fluidity of Cement Paste

Effect of Polycarboxylate-Type Superplasticizer on the Paste Fluidity Based on the Water Film Thickness of Flocs

Variations of Yield Stress of Fresh Cement Pastes in the Presence of Superplasticizer Highlighted by A Hydration Index

Rheological Behaviors of Fresh Cement Pastes with Polycarboxylate Superplasticizer

Influence Of Molecular Weight Of Pns Superplasticizers On The Properties Of Cement Pastes Containing Different Alkali Contents

Effect of Adding Electrolyte in Cement Paste on the Dispersing Force of Polycarboxylate-Type Superplasticizer

Influence of Amphoteric Polycarboxylate Copolymer Superplasticizer on Early Hydration of Portland Cement

Study on the Compatibility of Cement-Superplasticizer System Based on the Amount of Free Solution

Property of Water-Reducing and Crystallization on Superplasticize of the Concrete

The Properties of Cementitious Materials Superplasticized with Two Superplasticizers Based on Aminosulfonate–phenol–formaldehyde

Compatibility of Polycarboxylate Superplasticizer with Cements of Different Freshness

Influence of Soluble Alkali on the Compatibility of Cement and Aminosulphonate Based Superplasticizer

Effects of Comb-Shaped Superplasticizers with Different Charge Characteristics on the Microstructure and Properties of Fresh Cement Pastes

INFLUENCE OF SULFATE ON COMPATIBILITY OF CEMENT AND NAPHTHALENE SUPERPLASTICIZER

Influence of Alkali Sulfate and Superplasticizers on Bleeding Resistance of Cement Paste

Compatibility Between a Polycarboxylate Superplasticizer and the Belite-Rich Sulfoaluminate Cement: Setting Time and the Hydration Properties