Abstract:In this work, SrMn1-x Fe x O3-δ (x = 0–1) black ceramic pigments were synthesized by the solid-state method. The research explores the influence of calcination temperature and iron ion doping on the color properties of the pigments. Furthermore, the potential applications of SrMn1-x Fe x O3-δ pigments in ceramic glaze and heat-absorbing materials are also discussed. The findings reveal that the synthesized SrMnO3 pigment exhibits the lowest L*-value (22.30) at 1100 °C, although it displays a slight blue hue. To optimize the color properties of the SrMnO3 pigment, iron ion doping is employed. When the doping level of iron ions is 50 mol.% (i.e., x = 0.5), the L*-value of the SrMn0.5Fe0.5O3-δ pigment calcined at 1000 °C significantly decreases to 19.77, while the a*- and b*-values approach 0, resulting in a pure black color. This is attributed to the high surface roughness, low band gap energy, and substantial oxygen vacancies present in the SrMn0.5Fe0.5O3-δ pigment. The tinting mechanism of the SrMn1-x Fe x O3-δ pigment in the ceramic glaze is classified as "ion tinting", wherein the glaze color relies on the concentrations of Mn and Fe ions. When the pigment content reaches 36 wt.%, the L*-value of the glaze drops to 4.94, showing a deep black shade. Additionally, the SrMn0.5Fe0.5O3-δ pigment exhibits excellent sunlight absorption capabilities, with a near-infrared reflectance (R*) of only 5.04%. This research presents a black ceramic pigment with various advantages, such as simplified processing, affordability, environmental friendliness, and exceptional color performance.

Synthesis of strong-magnetic nanosized black pigment ZnxFe(3-x)O4

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

High-temperature Solid State Synthesis and Characterization in Magnetic and Transporting Properties of Zn_xFe_(3-x)O_4 Powder

Magnetite Fe3O4 Nanoparticles and Hematite Α-Fe2o3 Uniform Oblique Hexagonal Microdisks, Drum-Like Particles and Spindles and Their Magnetic Properties

A facile two-step hydrothermal route for the synthesis of γ-Fe 2 O 3 nanocrystals and their magnetic properties

Preparation and Characterization of MnFe2O4 by a Microwave-Assisted Oxidative Roasting Process

Systematic Study on the Synthesis and Magnetism Properties of Manganese Ferrite MnFe2O4 by an Oxidation Roasting Process

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

SrMn1-Fe O3- (x = 0–1) black ceramic pigment: Synthesis, color properties, and application

Synthesis and Characterization of Zn1-xCoxO Green Pigments with Low Content Cobalt Oxide

Synthesis and characterization of magnetite nanoparticles by a simple solvothermal method

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Preparation, Chromatic Properties Analysis and Proportioning Optimization of Co-Cr-Fe-Based Black Pigment

ZnFe2O4 Nanocrystals: Synthesis and Magnetic Properties

Preparation of Composite Nanoparticles of Fe-Zn Bioxide Using Surface Modification and Their Subsequent Characterization

Synthesis of Fe3O4 Nanoparticles and Their Magnetic Properties

Synthesis and Magnetic Properties of Mn-Zn Ferrite Nanoparticles

Synthesis of Nanometer-Size Maghemite Particles from Magnetite

High near-infrared reflectance Zn 1-x Mn x O yellow pigment prepared and properties by co-precipitation method

High Near-Infrared Reflectance Zn1-xMnxO Yellow Pigment Prepared and Properties by Co-Precipitation Method

Effective Synthesis of Green Nano‐sized Ceramic Pigments by Co‐doping Zn2+, Cr3+ and Sm3+ into the Cobalt‐aluminate