Abstract:The corrosion resistance and discharge activity of the rolled A represents aluminum, Z represents zinc, 9 and 1 represent their respective contents of 9% and 1% in the alloy magnesium alloy after electric pulse treatment show obvious patterns. Through research on its patterns and causes through immersion weight loss and electrochemical testing combined with microstructure observation results, it is found that the β‐Mg17Al12 phase and high‐energy grain boundary area in the alloy play a key role. In this article, a systematic investigation into the corrosion and discharge behaviors of as‐rolled a represents aluminum, Z represents zinc, 9 and 1 represent their respective contents of 9% and 1% in the alloy (AZ91) magnesium alloy after electro pulsing treatment (EPT), considering rolling deformations of 0% (as‐cast AZ91 magnesium alloy), 20%, 30%, and 40%, is presented. In this investigation, immersion weight loss tests, electrochemical tests, and other experimental methods are employed. In the results, it is revealed that the content of the β‐Mg17Al12 phase gradually decreases with increasing rolling deformation after EPT. Notably, the highest content of β‐Mg17Al12 phase and the most outstanding corrosion resistance are achieved with as‐cast AZ91 magnesium alloy. Furthermore, at low current densities (5 and 10 mA cm−2), the 30% rolling deformation exhibits superior discharge activity, while the discharge activity of the 40% rolling deformation is most excellent at high current densities (40 and 50 mA cm−2). The microstructure observations support these findings, highlighting the close relationship between the corrosion resistance and discharge activity of as‐rolled AZ91 magnesium alloy after EPT, and the content of the β‐Mg17Al12 phase and the area of high‐energy grain boundaries.

Study on the Effect of Cl- Concentration on the Corrosion Fatigue Damage in A Rolled Az31b Magnesium Alloy by Acoustic Emission

Recent progress in fatigue behavior of Mg alloys in air and aqueous media: A review

FATIGUE BEHAVIOR OF ROLLED AZ31B MAGNESIUM ALLOY IN AIR AND NaCl SOLUTION

In-situ monitoring of pitting corrosion of AZ31 magnesium alloy by combining electrochemical noise and acoustic emission techniques

Corrosion Fatigue Behavior of the High-Strength Magnesium Alloy AZ 80

Corrosion behavior of the electroplastic rolled AZ31 magnesium alloy in simulated sea water

Corrosion Behavior of AZ91D Magnesium Alloy in Acidic Solution of NaCl

Study on Acoustic Emission Characteristics of Fatigue Damage of A7N01 Aluminum Alloy for High-Speed Trains

The Effects of Corrosive Media on Fatigue Performance of Structural Aluminum Alloys

The Effect of Texture on the Corrosion Behavior of AZ31 Mg Alloy

Corrosion Fatigue Behaviors of Two Biomedical Mg Alloys-Az91d and We43-In Simulated Body Fluid

Corrosion and Discharge Behavior of As‐Rolled AZ91 Magnesium Alloy after Electro‐Pulsing Treatment

Exploring the Corrosion Performance of AZ31 Magnesium Alloy under Acidic and Alkaline Conditions

Evaluation of microstructural effects on corrosion behaviour of AZ91D magnesium alloy

Influence of load frequency and corrosive environments on fatigue behavior of as-extruded Mg–Zn–Zr–Nd alloy

Corrosion behavior of anodized AZ91D magnesium alloy in NaCl aqueous solution

Mechanical properties and wear-corrosion resistance of a new compound extrusion process for magnesium alloy AZ61

ELECTROCHEMICAL NOISE OF AZ31 MAGNESIUM ALLOY IN NaCI SOLUTION

A Study of the Effect of Additional Magnesium (Mg) on Erosion-Corrosion Resistance and Bending Strength in Aluminum A383 Alloy

Effects of grain size and Al-Mn phase on the corrosion performance of hot-rolled AZ31 magnesium alloy

Effect of grain refinement induced by wire and arc additive manufacture (WAAM) on the corrosion behaviors of AZ31 magnesium alloy in NaCl solution