Preparation of AI-Zn-Mg-Sc-Zr alloy plate and its microstructure-properties evolution
Zhi-min YIN,Ying DENG,Kai ZHAO,Jia-qi DUAN,Bei TANG,Zhen-bo HE,Yong-yi PENG,Feng JIANG,Qing-lin PAN
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2011.10.027
2011-01-01
Abstract:The evolution of microstructure and properties of Al-5.4Zn-2.0Mg-0.25Cu-0.1Sc-0.1Zr under different processing and heat treatment conditions was studied using mechanical properties measurement and electron microscopy. The results show that, under semi-continuous casting conditions, at grain boundaries there is some segregation which is bearing Zn, Mg non-equilibrium phases and indissoluble impurity phases containing Fe, Si and Mn elements. After the homogenization at 470°C for 12 h the non-equilibrium phases dissolve into matrix completely and only small amounts of indissoluble phases still exist. At the same time, the solid solution matrix precipitates nano-scaled Al 3(Sc, Zr) dispersoid particles. The proper homogenization treatment processing of the ingot is at 470°C for 12 h. During the hot deformation of ingot, with the increase of deformation temperatures, the strength decreases, the elongation increases firstly and then decreases. Between 350°C and 400°C the alloy is of a more stable deformation characteristics and this is the suitable deformation temperature range for this alloy. After solutioning at 470°C for 1 h lots of non-equilibrium phases formed during hot rolling dissolve into the matrix. The precipitation sequence of the alloy during aging is described as follows: supersaturated solid solution (α)→GP zones→metastable η' phase→η phase. The suitable solution-aging treatment processing of the studied alloy is solution-treated at 470°C for 1 h, followed by water quenching and then aged at 120°C for 24 h. Under this condition, the ultimate tensile strength, yield strength and elongation of the studied alloy plate could reach 533 MPa, 494 MPa and 15%, respectively. The strengthening mechanism of the studied alloy is precipitation strengthening of fine η' phase, subgrain strengthening and dispersion strengthening caused by Al 3(Sc, Zr) dispersoid particles.