Abstract:The oxidation behaviors of molten WE43 (Mg–4.32Y–2.83Nd–0.41Zr, wt%) in resin-sand mold atmosphere were systematically investigated. X-ray diffraction, X-ray photoelectron spectroscopy, and scanning electron microscopy analyses were employed to identify the phase compositions and microstructures of surface oxide scale. The initial oxide scale characterized by a three-layer structure mainly consisted of MgO, Y2O3, and ZrO2 and then transformed to Y2O3 layers covered by porous MgO after holding at high temperatures. CALPHAD method was used to analyze the oxidation process, and the calculated phase diagrams agreed well with the experimental results. A selective oxidation model was established based on thermodynamic and kinetic analysis to describe the structure transformation of oxide scale in detail. The initial oxidation was controlled by inward diffusion of oxygen due to the protection of surface Y2O3. However, the oxide scale was not protective after long-term oxidation or at temperatures higher than 1073 K due to the oxide fracture, which can be attributed to the increase in stress caused by inner Y2O3 layer growth. Based on experimental results, the oxide growth stress parameter C was estimated to be 0.0013 and 0.0026 for 1023 and 973 K, respectively. This work reveals the underlying oxide growth and fracture mechanisms of molten Mg–Y alloy in mold, and provides guidance for preventing the ignition of magnesium alloys during casting processes.

Oxidation Behavior Of Az31 Magnesium Alloys With Yttrium Ion Implantation

Micro-arc Oxidation Behaviors of AZ91D Magnesium Alloy in Different Electrolytes

Improvement in corrosion resistance and biocompatibility of AZ31 magnesium alloy by NH<sub>2</sub><SUP>+</SUP> ions

The air oxidation of yttrium ion implanted zircaloy-4 at 500°C

Improvement in corrosion resistance and biocompatibility of AZ31 magnesium alloy by NH2+ ions

Retardation of Surface Corrosion of Biodegradable Magnesium-Based Materials by Aluminum Ion Implantation

The behavior of yttrium implants in H13 steel under high temperature oxidation

Corrosion resistance and biocompatibility of carbon ion implanted AZ31B magnesium alloy

In-mold Oxidation Behavior of Mg–4.32Y–2.83Nd–0.41Zr Alloy

Influence of Implanted Aluminum Ions on the Oxidation Behavior of M5 Alloy at 500°C

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Modification of Corrosion Resistance by Yttrium Ion Implantation of 30 4L Stainless Steel

The Influence of Yttrium Ion Implantation on the Oxidation Behavior of Zircaloy-4 at 600 °C

Controlled surface mechanical property and corrosion resistance of ZK60 magnesium alloy treated by zirconium ion implantation

Influence of Anodic Oxidation on the Organizational Structure and Corrosion Resistance of Oxide Film on AZ31B Magnesium Alloy

Corrosion Resistance and In Vitro Biological Properties of TiO2 on MAO-Coated AZ31 Magnesium Alloy via ALD

Influence of Aluminum Ions Implanted on Oxidation Behavior of ZIRLO Alloy at 500 °C

Improvement in corrosion resistance and biocompatibility of AZ31 magnesium alloy by NH+2 ions

Influence of Biocompatible Metal Ions (ag, Fe, Y) on the Surface Chemistry, Corrosion Behavior and Cytocompatibility of Mg-1ca Alloy Treated with Mevva

Study on Micro-arc Oxidation of Mg-Zn-Y-Nd-Ca Magnesium Alloys

Effects of Cr, Y and Nb Ion Implantation on Oxidation Behavior of Γ-Tial at 1000℃