Research on nano-Ti modified polymer by high energy milling

Jusheng Zhang,Jifeng Zhang,Zhigang Liu,XueTian Gao,Qingna Huang,GuangHui Xu,Xiaojuan Pan,Ming Lu
DOI: https://doi.org/10.3321/j.issn:1002-185x.2007.12.031
2007-01-01
Rare Metal Materials and Engineering
Abstract:Modified polymer by nano-Ti was prepared by high energy ball milling and was dispersed in resins to prepare anti-corrosion coatings. XRD, XRF, TEM, SEM and XPS were used to analyses the samples. The experimental results show that the Ti powder in the black muddy samples were dispersed uniformly and whose diameters were from 50 nm to 80 nm, when the ratio of balls to materials weights was 3:1. The Ti powders were packed by polymer. No change of the coating film took place, after being immerged into 30% H2SO4 solution, 10% NaOH solution and 3.5% NaCl solution for 4320, 6000, 2000 h, it means that the nano-Ti modified polymer greatly improved the corrosion resistance of the coatings.