Dispersion Property of Nano-TiO2 and Its Effect on Modified Automobile Finish Coating

Ya-li LIU,Zhan-feng YU,Yin-xiang CAO,Shu-xue ZHOU,Bo YOU,Li-min WU
DOI: https://doi.org/10.3969/j.issn.1001-1560.2005.11.002
2005-01-01
Abstract:For the purpose to improve the down-flop effect and antiwear of automobile gleam coating,the dispersion property of nanometer TiO_2 particles and its influence on the coating performances were studied.Nano-TiO_2 was pretreated by ultrasonic dispersion,and the special dispersant and content were chosen.TiO_2 slurry was prepared by wet grinding method of cycle stirring ball mill,and then was added into automobile coating.Results show that ultrasonic pretreatment can decrease the size distribution of slurry,and the stability of slurry is best with using 0.8% dispersant.The average size of slurry is 110~120 nm,the transmittance of slurry is above 90% in visible zone and low than 5% in UV zone,and the slurry is transparent with good UV resistance.Metallic gleam coating with obvious down-flop effect can be obtained by mixing the slurry and aluminum powder to a scale.The nano-TiO_2 can improve the flexible of coating to some extend besides the gloss retention and wear resistance but no effect for the shock resistance.
What problem does this paper attempt to address?