Abstract:Cold crucible induction melter (CCIM) technology has been widely used in melting of non-metallic refractory materials with a high melting point and a requirement of high purity. This paper discusses the application of the CCIM technology in melting of reactor corium (simulated as zirconium oxide in this experiment).In this experiment, the power supply is set at constant power control mode, with a design frequency of similar to 100 kHz and a total output power of similar to 400 kW. The cold crucible consists of copper tubes and a stainless bottom plate which has a dimension of 220 mm in diameter and 420 mm in height. The crucible is charged with zirconium oxide (ZrO2) powder and surrounded by a set of water-cooling induction coils which is designed shorter than the crucible in order to reduce energy loss in the water-cooling bottom plate. The top of the crucible and the coils are at the same height. A Zirconium ring is used to initiate heating process. similar to 50 kg ZrO2 powder is used for each experiment. Electrical variables of the induction melter and temperature of the melt are detected and recorded in the entire heating process.For the result, almost 3/4 of the ZrO2 powder is melt and a thin crust (2-3 mm) is generated between the melt and the crucible. To be specific, the ZrO2 powder above the bottom of the induction coils is melt, but others are not. In the melting process, the maximum surface temperature of the melt has reached 2230 t. Furthermore, for better understanding of the relationship between the melting process and the changing process of the electrical variables, an equivalent circuit of the heating system is established and analyzed. It can be concluded that some electrical variables such as the quality factor (Q) of the induction coils and the practical frequency can reflect melting status. The conclusion is confirmed by the records transmitted by sensors in the melting process. By comparison between the recorded data and the melting status, it is clear that the Q value can be accurately used in indicating the melting status due to its obvious change in the entire melting process. As the melting pool becoming larger, the Q value tends to be smaller. In contrast, the practical frequency becomes higher as the melt becoming larger. Furthermore, both of them are not influenced by the output power. In addition, the output current and the output voltage also can be used to describe the melting status. In specific, a larger melting pool corresponds to a lower output current and a higher output voltage.

Research and Development of Cold Crucible Melting and Casting Technology

Development and Advances in Cryogenic Treatment Technique and Device

Experimental Analysis of the Aluminium Melting Process in Industrial Cold Crucible Furnaces

Preparation of a (Ca,Sr,Ba)ZrO3 Crucible by Slip Casting for the Vacuum Induction Melting of NiTi Alloy

Microstructure refinement and improvement of mechanical properties of Ti46Al8Nb0.9B alloys by electromagnetic cold crucible continuous solidification

Application of Cold Crucible Technique in the Nuclear Waste Treatment

High-throughput analysis of Al and Nb effects on mechanical behaviour of TiAl alloys using electromagnetic cold crucible continuous casting

Research and Development on Slurry of Precision Casting Titanium and Ti-alloy Abroad

Interaction Between CA6-MA Crucible and Molten Wrought Ni-based Superalloys

Experimental Study Of Performance Of Cold Crucible Induction Melter In Melting Corium Simulant

Interaction between CA 6 -MA crucible and molten wrought Ni-based superalloys

Anti-corrosion AlN ceramic crucible with excellent thermal shock resistance for induction melting of TiAl alloy

A novel potential ceramic material for melting Ti6Al4V alloy: A solid solution of BaZrO3 and CaZrO3

Interactions between TiAl alloys and yttria refractory material in casting process

A review of electromagnetic stirring on solidification characteristics of molten metal in continuous casting

Effects of cooling rates on microporosity in DC casting Al-Li alloy

Numerical simulation study on solidification process of titanium slab ingot by electron beam cold hearth melting

Characterization and mechanism analysis of interaction between Inconel 713C superalloy and a novel crucible-shell "integrated" mold

The Study on Interaction Mechanisms Between Ti48al2cr2nb Alloy and Y2o3 Ceramic Crucibles with Good Thermal Shock Resistance: Assessing a Novel, Cost-Effective Approach to the Preparation of High-Performance Tial Alloys

Scalable manufacturing of the Al-based master composites containing TiB 2 and TiC particles and their modification effect on the hot cracking of rapidly solidified Al alloys

Sintered crucible coating for highly under-cooled Cu-Ni-Fe alloys