Capacity Fading of LiCr 0.1 Mn 1.9 O 4 /MPCF Cells at Elevated Temperature

Jiangang Li,Xiangming He,Maosong Fan,Chunrong Wan,Changin Jiang,Shichao Zhang

DOI: https://doi.org/10.1007/s11581-006-0019-1

IF: 2.961

2006-01-01

Ionics

Abstract:Capacity fading of LiCr 0.1 Mn 1.9 O 4 /MPCF (mesophase pitch-based carbon fiber) cells was investigated at elevated temperature (55 °C). The cells showed very fast capacity fading, keeping only 60% of capacity retention at the 100th cycle at 55 °C. The cycled electrodes and the electrolyte were analyzed using electrochemical test, inductively coupled plasma, and X-ray diffraction. Results of the analyses indicated that LiCr 0.1 Mn 1.9 O 4 exhibited good effects on restraint of Mn dissolution and stabilization of structure at 55 °C. The cycled LiCr 0.1 Mn 1.9 O 4 electrode and the cycled MPCF electrode presented good electrochemical performance again with fresh electrolyte. Therefore, it was proposed that the cycling fading of LiCr 0.1 Mn 1.9 O 4 /MPCF cells was mainly caused by decomposition of electrolyte upon LiCr 0.1 Mn 1.9 O 4 electrode during cycling. It was found that the decomposition of electrolyte led to the formation of a surface layer comprised of Li 2 CO 3 , Li x PF y , CH 3 OCO 2 Li or (CH 2 OCO 2 Li) 2 , polymeric ether etc. The formation of this film consumed active lithium ions, leading to fast capacity fading of LiCr 0.1 Mn 1.9 O 4 /MPCF cell at elevated temperature.