Extreme fast charging and stable cycling of LiMn2O4 – Li4Ti5O12 lithium batteries by suppression of cathode phase changes

Binayak Roy,Urbi Pal,Darcy Simondson,Cuong Nguyen,Brittany Kerr,Rosalie Hocking,Danah Al-Masri,Patrick Howlett,Maria Forsyth,Mega Kar,Douglas MacFarlane

DOI: https://doi.org/10.26434/chemrxiv-2023-mt0wm-v2

2023-12-21

Abstract:Extreme fast charging (XFC, i.e., achieving at least 80% state of charge within 15 minutes) remains as a high-desirability criterion for next-generation lithium batteries. While the anodes, e.g., graphite and lithium, have been historically acknowledged as critical hurdles for fast-charging batteries, the stability of the cathodes under sustained high-rate cycling has not been well studied. In this work, we have investigated the fast cycling (10 - 15 minutes charging time) of LiMn2O4 (LMO) under practical conditions (90% loading of cathode material with an areal capacity of 1 mAh/cm2). We find through advanced characterisation that in the presence of LiPF6-based electrolyte, the high rate cycling of LMO causes a cascade of bulk LiMn2O4→LiMnO2 phase changes, accompanied by oxygen release, initiating electrolyte degradation. Together, these factors play a compounding role in the capacity loss during cycling, even with high-rate compatible anodes, e.g., Li4Ti5O12 (LTO). The combination of a commercial, high-capacity, micro-structured LMO cathode and novel electrolyte, prepared by using a novel lithium salt, lithium 1,1,1,3,3,3, (tetrakis) hexafluoroisopropoxy borate, in a mixture with commercial electrolyte, overcomes these limitations. The performance improvement is attributed to the synergy between the unique cathode structures and the formation of a facilitative boron-rich cathode electrolyte interface. Cycling of the LMO|LTO cells show 98 mAh/g initial discharge capacity at 4C-4D cycling with the novel electrolyte with 91% capacity retention after 1500 cycles, while charging to 90% of total capacity in 10 minutes. This work, for the first time, demonstrates the long-term stability of practical high loading LMO-LTO based Li-ion battery under XFC conditions, which has been upscaled and reproduced in a single-layer pouch cell.

Chemistry

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: under the condition of extreme fast charging (XFC, that is, reaching at least 80% of the state of charge within 15 minutes), how to achieve the stable cycling of LiMn₂O₄ (LMO) - Li₄Ti₅O₁₂ (LTO) lithium - ion batteries. Specifically, the research focuses on:

1. **Suppressing phase transformation of cathode materials**: During high - rate cycling, the LMO cathode material will undergo a series of phase transformations (such as from LiMn₂O₄ to LiMnO₂), accompanied by oxygen release, which leads to electrolyte degradation and capacity fading. These problems are particularly significant under high - rate cycling conditions.

2. **Improving the long - cycle stability of batteries**: The research aims to form a stable cathode - electrolyte interface (CEI) by improving the electrolyte formula, especially by using new lithium salts (such as LiBHFip), so as to suppress phase transformation and oxygen release, and then improve the long - term stability of the battery under high - rate cycling.

3. **Meeting the requirements of practical applications**: The research not only focuses on the performance improvement under laboratory conditions, but also emphasizes the feasibility in practical application scenarios (such as 90% active material loading, 1 mAh/cm² areal capacity), ensuring that the research results have practical value.

### Specific problem description

- **Limitations of traditional electrolytes**: Traditional LiPF₆ - based electrolytes will cause irreversible phase transformation of the LMO cathode material during high - rate cycling, generate oxygen and cause electrolyte degradation, and finally lead to rapid battery capacity fading.

- **Design and verification of new electrolytes**: The research introduced a new hybrid - salt electrolyte (HRMSE). By adding LiBHFip to improve the electrolyte performance, especially under high - rate cycling conditions, it can effectively suppress the phase transformation and oxygen release of the LMO cathode material, thereby improving the cycling stability and life of the battery.

- **Performance in practical applications**: The research shows that under practical application conditions (such as 90% active material loading, 1 mAh/cm² areal capacity), the LMO - LTO battery using the new electrolyte can maintain good performance under high - rate cycling of 4C - 4D, with an initial discharge capacity of 98 mAh/g, and can still maintain a capacity retention rate of 91% after 1,500 cycles.

Through these studies, the authors hope to provide a feasible technical solution for the next - generation high - performance, fast - charging lithium - ion batteries, especially for applications in high - power devices and electric vehicles.