Effects of Low-Temperature Pre-Cycling on High-Temperature Degradation of Lithium-Ion Cells
Muriel Carter,Pragati Poudel,Megan Gober,Boryann Liaw,George J. Nelson,Guangsheng Zhang,Boryann (Bor Yann) Liaw
DOI: https://doi.org/10.1149/ma2023-012624mtgabs
2023-08-28
ECS Meeting Abstracts
Abstract:Lithium-ion (Li-ion) batteries suffer accelerated degradation when the operating temperature is beyond the optimal range 1, 2 , about 20 °C to 35 °C. At lower temperatures and higher temperatures, lithium plating and solid-electrolyte interface (SEI) growth are dominating degradation mechanisms, respectively 1 . A previous work by our group 3 showed interestingly that pre-cycling Li-ion cells at 5 °C reduced degradation during cycling at higher temperatures of 45 °C and 60 °C. The observation suggested that low-temperature pre-cycling has significant effects on high-temperature degradation of Li-ion cells. The previous work was based on small cells that consisted of a single pair of electrodes. To confirm if the phenomenon also exists in large cells that consist of multiple pairs of electrodes, commercially available 3-Ah pouch cells are tested. It is found that pre-cycling of these large cells at 5 °C also significantly reduces their degradation at 45 °C. However, this effect is observed only when the cells are compressed. Without compression, cells pre-cycled at 5 °C degrade much faster than baseline cells cycled only at 45 °C. Further analysis of the results, such as cell internal resistance analysis and electrochemical impedance spectroscopy, is performed to better understand the effects of low-temperature pre-cycling on high-temperature degradation behaviors of Li-ion cells. References: T. Waldmann, M. Wilka, M. Kasper, M. Fleischhammer and M. Wohlfahrt-Mehrens, Journal of Power Sources , 262 , 129 (2014). F. Leng, C. M. Tan and M. Pecht, Scientific Reports , 5 , 12967 (2015). P. Poudel, Z. Du, B. Liaw, T. Iriyama and G. Zhang, ECS Meeting Abstracts , MA2022-01 , 443 (2022).