LiNi0.5Co0.2Mn0.3O2/graphite batteries storing at high temperature: Capacity fading and raveling of aging mechanisms

Lingling Zhang,Jilong Liu,Lei Du,Peng Fan,Xing Xu,Yulin Ma,Pengjian Zuo,Bin Qu,Geping Yin,Qiang Fu

DOI: https://doi.org/10.1016/j.jpowsour.2021.229858

IF: 9.2

2021-06-01

Journal of Power Sources

Abstract:The effects of storage on the aging mechanisms of the battery have attracted a lot of attention. In practice, the battery for electric vehicles (EVs) can undergo short periods of higher temperature storage. Therefore, the widely-used LiNi0.5Co0.2Mn0.3O2/graphite batteries are stored at different temperatures (25 °C, 60 °C, and 70 °C) for 15 days, and then cycled under normal ambient environment. The aging mechanisms are analyzed by electrochemical characterizations and post-mortem analysis. The aging rate and mechanisms of batteries stored at a lower temperature (e.g. 25 °C and 60 °C) almost remain unchanged. According to the results of quantitative analysis, although the aging of batteries stored at a higher temperature (e.g. 70 °C) is attributed to the increased polarization, the underlying reasons might be different. Increased polarization at higher temperature is primarily ascribed to cathode decay in addition to the anode decay. The thickened cathode surface layer and increased cation disorder hinder the lithium ion diffusion, contributing to the cathode decay. Based on these test results, it is proposed that batteries subjecting to lower storage temperature for short time can have a second life while those at higher storage temperature should be discarded.

energy & fuels,materials science, multidisciplinary,electrochemistry,chemistry, physical

What problem does this paper attempt to address?

The paper primarily investigates the cycling performance and aging mechanisms of LiNi0.5Co0.2Mn0.3O2/graphite batteries stored for 15 days at different temperatures (25°C, 60°C, and 70°C) under ambient conditions. The core issue of the study is to explore the impact of high-temperature storage on battery performance and propose corresponding aging mechanisms.

Specifically, the study found that:
1. Batteries stored at lower temperatures (such as 25°C and 60°C) show almost no change in aging rate during ambient cycling.
2. High-temperature storage (such as 70°C) leads to increased battery polarization, mainly due to the degradation of the cathode material and partial degradation of the anode material.
3. High-temperature storage causes the cathode surface layer to thicken and increases cation disorder, hindering lithium-ion diffusion and resulting in decreased cathode performance.
4. Based on the test results, the study suggests that batteries stored at lower temperatures for short periods can continue to be used, while those stored at higher temperatures should be discarded.

Through these studies, the paper aims to provide a theoretical basis for the design of battery management systems for electric vehicles, predict battery life, and assess the feasibility of secondary use.