Abstract:As an important mechanical property index, the interfacial bonding properties between coating and substrate are key factors in determining the corrosion resistance and reliability of the system. In this paper, the corrosion resistance performance and interfacial bonding properties of the Zn/Zn–Al multilayer coating/steel substrate system were studied. Neutral salt spray tests and electrochemical tests were conducted to evaluate the corrosion resistance of the coatings. Meanwhile, the three-point bending test with the acoustic emission (AE) technique was used to study the interfacial bonding properties of the multilayer coating/substrate systems. As a comparison, these tests were carried out on a Zn monolayer coating/substrate system and a Zn–Al monolayer coating/substrate system. The corrosion test results showed that the superposition of the Zn/Zn–Al coating/substrate system with different grain sizes hinders the transport path of corrosive ions, resulting in rust spots appearing later in the multilayer coating/substrate system than in the monolayer coating/substrate system. Given the increase in coating thickness, the defects, porosity, and corrosion through the holes of the coating increase, which aids in the corrosion process and reduces the corrosion resistance of the coating. The interfacial bonding strength of the system was analyzed using fracture toughness. The test results showed that the extent of the depreciation of the fracture toughness of the multilayer coating/substrate system before and after corrosion is lower than that of the monolayer coating/substrate systems. The interfacial bonding properties of the multilayer coating/substrate system are better than that of the monolayer coating/substrate systems because of the good material matching and dislocation effect between the multilayer coatings.

Bonding Mechanism of Zn Powder in Mechanically Deposited Zn Coating

The Effect of Suspended Particles on the Corrosion Resistance of Electrodeposited Zinc Powders

Study on Microstructure and Properties of Mechanically Deposited Zn-Sn Coating

Effect of Impact-Induced Melting on Interface Microstructure and Bonding of Cold-Sprayed Zinc Coating

Formation of metastable phases in cold-sprayed soft metallic deposit

Fabrication of Zinc Coatings on Alumina Balls from Zinc Powder by Mechanical Coating Technique and the Process Analysis

A Novel Bond Coat with Excellent Adhesive Strength Deposited by Plasma-Spraying of Mo-Clad Core-Shell-Structured Metal Powders

Experimental Investigation of Hot Forming of Zn‐Coated Hot‐Stamping Steel

Influence of Metal Properties on the Formation and Evolution of Metal Coatings During Mechanical Coating

Influence of intermittent air introduction on formation of Zn films by mechanical coating technique

Surface Modification With Zinc and Zn-Ni Alloy Compositionally Modulated Multilayer Coatings

Investigation of Corrosion Resistance and Interfacial Bonding Properties of Zn/Zn–Al Multilayer Coating/Steel Substrate System

The Bond Strength of Al–Si Coating on Mild Steel by Kinetic Spraying Deposition

Fabrication and characterization of zinc-coated aluminum particle joining materials via zincate treatment

Solving the Bonding Problem of the Ni Thin Coating with the Ultrasonic Assisted Electrochemical Potential Activation Method

Fabrication and Characterization of Ni–Zr Composite Coatings Using Electrodepositing Technique

Preparation of Cu-ZrW2O8 Composite Coatings by Electric Deposition

Effect of bonding process on the microstructures and strength of W/steel joints with a W-Cu-Ni interlayer

Preparation of Cu Coated ZrW<sub>2</sub>O<sub>8</sub> Composite Powders Via Heterogeneous Precipitation Process

Potentiodynamical deposition and corrosion behavior of thin Zn-Sn coatings with layered structure and varied composition from deep eutectic solvent

An Effective Approach for Creating Metallurgical Self-Bonding in Plasma-Spraying of Nicr-Mo Coating by Designing Shell-Core-Structured Powders