Abstract:Low-temperature epitaxy of ZnO films was carried out on both Si(00 1) and silica substrates by reactive e-beam evaporation. Growth temperature was varied between 100 degrees C and 450 degrees C. The optimal growth temperatures were between 200 degrees C and 300 degrees C for Si(00 1) substrates and 300 degrees C and 350 degrees C for silica, respectively. Structural and optical characteristics grown on both of Si and silica were compared by measurements of X-ray diffraction, Raman scattering and photoluminescence excitation (PLE) spectroscopy. X-ray diffraction showed the ZnO films grown both on Si(00 1) and silica substrates were all highly c-axis-oriented and their linewidth of (002) diffraction peak is significantly smaller than that measured from ZnO films deposited by magnetron sputtering. However, Raman scattering demonstrated the presence of excess zinc in the ZnO/silica structure. PLE measurements exhibited the sharp band-absorption edge and exciton absorption in the ZnO films on Si(00 1) and poor optical properties of ZnO on silica. PLE also revealed that the absorption characteristic near the band edge remarkably changed with the variation of oxygen content in the ZnO lattice while X-ray diffraction showed that the crystalline structures of ZnO films grown under different O-2 pressure almost remained unchanged. The underlying mechanism of low-temperature epitaxy of high-quality ZnO films and its applications in electronic and optoelectronic devices are discussed. (C) 2000 Elsevier Science B.V. All rights reserved.

LOW-TEMPERATURE SYNTHESIS OF NOVEL ZINC OXIDE SINGLE-SIDED COMB-LIKE STRUCTURE

Supersaturation-controlled synthesis of two types of single-sided ZnO comb-like nanostructures by thermal evaporation at low temperature

Rod-Like Zinc Oxide Constructed by Nanoparticles: Synthesis, Characterization and Optical Properties

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

Controllable Synthesis and Optical Properties of Novel ZnO Cone Arrays Via Vapor Transport at Low Temperature

Low-temperature synthesis of ZnO nanonails

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

From Zinc Nanowires to Zinc Oxide Nanowires: A Low Substrate-Temperature Approach

Low Temperature Synthesis and Optical Properties of Small-Diameter ZnO Nanorods

Low-Temperature Epitaxy Of Zno Films On Si(001) And Silica By Reactive E-Beam Evaporation

Low-Temperature Growth of Zno with Controllable Shapes and Band Gaps

Tempererature-Controlled Growth Of Zno Nanostructures: Branched Nanobelts And Wide Nanosheets

On the formation of well-aligned ZnO nanowall networks by catalyst-free thermal evaporation method

Catalyst-free Synthesis of ZnO Nanowire Arrays on Zinc Substrate by Low Temperature Thermal Oxidation

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Synthesis of ZnO Nanowires for Thin Film Network Transistors

Low-temperature epitaxy of ZnO films on Si(0 0 1) and silica by reactive e-beam evaporation

Synthesis of ZnS hollow nanoneedles via the nanoscale Kirkendall effect

Synthesis and Mechanism of 1D ZnO Based on Alkaline Dissolution‐Conversion Strategy of High Stable and Soluble Ɛ‐zn(oh)2

Low temperature growth and properties of ZnO nanorod arrays