Abstract:Bimetallic composites have a wide range of application prospects in various industries. Different bonding temperatures, as one of the influencing factors, directly affect the bonding effectiveness as well as the performance and application of the materials. Using metallurgical bonding techniques ensures a strong bond at the interface of bimetallic materials, resulting in high-quality composite pipe billets. This paper describes an Incoloy825/P110 steel bimetal composite material made by the solid-liquid composite method. By utilizing ProCAST 14.5 software for simulation and deriving theoretical formulas, an initial range of temperatures for bimetallic preparation has been tentatively determined. And this temperature range will be utilized for on-site experiments to prepare bimetallic samples. After the preparation process is completed, samples will be selected. The influence of the external mold temperature on the interface bonding of Incoloy825/P110 steel solid-liquid composite material is studied using an ultra-depth three-dimensional morphology microscope and a scanning electron microscope. Through research, the optimal preheating temperature range for the solid-liquid composite outer mold of Incoloy825/P110 bimetallic composite material has been determined. The casting temperature of the inner mold has a significant impact on the interface bonding of this bimetal composite material. As the casting temperature of the inner mold increases, the interface thickness gradually increases. At lower temperatures, the interface thickness is lower and the bonding is poorer. At higher temperatures, melting may occur, leading to coarse grains at the interface. When the temperatures of the inner and outer molds are within a certain range, a new phase appears at the interface. Indeed, it increases the strength of the interface bonding. Due to co-melting of the bimetal near the interface, element migration occurs, resulting in increased Ni and Cr content at the interface and enhanced corrosion resistance.

Centrifugal Casting Process and Interface Control of Steel/Iron Bimetal Composite

Processing and Wear Resistance of Carbon-Steel/High-Cr-Cast-Iron Bimetal Composite

Initial Discussion of Centrifugal Casting Process for Dual-metal Clad Tube in Carbon Steel-High chromium Casting Iron

Interfacial characteristics of combined carbon steel and stainless steel based on casting process

Analysis of Heat Transport and Thickness of Bimetal Composition Layer Between Low-Alloy Steel and High-Chromium White Cast Iron

Research on the Solid-Liquid Composite Casting Process of Incoloy825/P110 Steel Composite Pipe

Laser Cladding Fe/FeCr Coatings on Continuous Casting Cu Mold

Mold Filling and Solidification of Bimetal Roller Sleeve for Coal Grinding Mill During Centrifugal Composite Casting Process

Microstructure and Formation Mechanism of Two-Liquid Bimetal Composite Interface

Process Optimization of Dual-Liquid Casting and Interfacial Strength–Toughness of the Produced LAS/HCCI Bimetal

Bonding of Cast Iron-Aluminum in Bimetallic Castings by High-Pressure Die Casting Process

Casting Technology Research on the Centrifugal Composite Roller of Three Layers Based on ANSYS

Fabrication of WC Particles Reinforced Iron Matrix Surface Composites by Centrifugal Casting

Interface and wear characteristics of high-Cr cast iron matrix composite reinforced with cemented carbide particles

The pre-hot dipping effects on the bimetal casting of nitriding steel sleeve into the Al-Si matrix

Microstructures of carbon steel/high chromium iron composites prepared by centrifugal casting-hot rolling process

Effect of Two-liquid Bimetal Wear Resistance Plate Thickness on Microstructures and Properties of Composition Layer

Processing of Al/Cu Bimetal Via a Novel Compound Casting Method

Study on Liquid-Liquid Bimetal Composite Casting Hammers

Interface area morphology and formation mechanism of copper/steel composite prepared by the hot-dip casting

Achieving Metallurgical Bonding in Aluminum/Steel Bimetallic Castings