Abstract:Copper/steel composite is a kind of composite with excellent performance and broad application prospects. In this paper, the micro-morphology and structure of the interface of copper/steel composite prepared by the hot-dip casting were observed by scanning electron microscope and transmission electron microscope, and the formation mechanism of the interface area was explored. The results show that the hot-dip casting temperature has a great influence on the micro-structure and morphology of the copper/steel interface area. When the hot-dip casting temperature is lower than 1125 °C, the copper/steel interface area is basically in a straight line. Even if the hot-dip casting time is extended, the interface characteristics change little. At 1100 °C, the copper-rich phase precipitated at the interface area is the coherent precipitates of Cu and BCC-Fe, with the crystal orientation and the diameter about 10 nm ~ 30 nm. When the hot-dip casting temperature reaches 1150 °C, the copper/steel interface area begins to appear new micro-morphology, and the range of new micro-morphology becomes larger and larger with the increase in the hot-dip casting temperature and the extension of the hot-dip casting time. At 1200 °C, the copper-rich phase precipitated at the interface is the coherent precipitates of FCC-Cu and FCC-Fe, with the crystal orientation and the size similar to that at 1100 °C. In the process of the hot-dip casting, the formation of the copper/steel interface area experienced three stages: the co-temperature of copper/steel and the wetting of copper liquid on solid steel, the formation and transformation of the solid–liquid mixed layer between steel and copper liquid and the evolution stage of the liquid–solid mixed layer during cooling and solidification. This kind of interface zone with gradual structure tightly connects the steel matrix and solidified copper together, to form a copper/steel composite with strong bonding.

Microstructures of carbon steel/high chromium iron composites prepared by centrifugal casting-hot rolling process

Achieving Homogeneous Fe Distribution and High Strength in Cu-Fe Composite Consolidated by Powder Rolling

Microstructure and Mechanical Properties of High-Chromium Cast Iron/Low-Carbon Steel Composite Prepared by Hot Rolling Process

Effect of Hot-Rolling Deformation on Microstructure and Sliding Wear of High-Chromium Cast Iron

Fabrication of a Composite Material of High‐Chromium Cast Iron Dispersed in Low‐Carbon Steel by Hot‐Rolling Process

Influence of hot rolling + heat treatment on microstructure and mechanical properties of NM500/Q345/NM500 composite plate

Microstructure and tensile behavior of high-chromium cast iron/low-carbon steel composite fabricated by accumulative roll-bonding

FABRICATION AND PROPERTIES OF HIGH-CHROMIUM CAST IRON DISPERSED STEEL MATRIX COMPOSITE

Interfacial reaction behavior of titanium/steel composite plate formed by cold-hot rolling

Interfacial microstructure and strengthening mechanism of stainless steel/carbon steel laminated composite fabricated by liquid-solid bonding and hot rolling

Microstructural evolution of austenite under conditions simulating thin slab casting and hot direct rolling

Interfacial microstructure and mechanical properties of stainless steel clad plate prepared by vacuum hot rolling

Interface area morphology and formation mechanism of copper/steel composite prepared by the hot-dip casting

Study on Centrifugal Compound Casting-hot Extrusion-Cold Rolling Process for Composite Pipe

The Effect of a Coating Sprayed Using Supersonic Flame Coating Technology on the Mechanical Properties and Interface Structure of a Thick Steel/Aluminum Composite Plate during Hot Rolling

Bonding mechanism and preparation process of titanium/iron composite thin sheet by non-vacuum rolling

Microstructure and properties of W Cu composites reinforced by in-situ generated WC

An innovative process of clad teeming and rolling for preparing stainless steel/carbon steel clad plate

Microstructure and mechanical properties of in-situ Ti 5 Si 3 /TC4 composites via spark plasma sintering and hot rolling

Effects of sintering temperature on interface microstructure and element diffusion of WC-Co-Ni-Fe/high-speed steel composites

Effects of the Rolling Temperature on Microstructure and Mechanical Properties of 2cr13/316l Laminated Composites Prepared by Accumulative Roll-Bonding (ARB)