Preparation and Properties of ZTA + WC Particles/Hypereutectic High Chromium Cast Iron Composites
Ping Li,Xin Jin,Yingfan Zhao,Shuang Liu,Weiping Tong
DOI: https://doi.org/10.1007/s11665-024-10172-8
IF: 2.3
2024-10-02
Journal of Materials Engineering and Performance
Abstract:Millimeter-sized ZTA (zirconia toughened alumina) particles + WC (tungsten carbide) particles reinforced hypereutectic high chromium cast iron (H-HCCI) composites were prepared by liquid phase sintering. The volume fraction, stacking method and sintering process of the reinforced particles in the composites were designed. The interfacial bonding mechanism between the reinforcements and the matrix in the composites was systematically discussed. The results show that when the sintering temperature is 1380 °C, the volume percentage of ZTA particles, WC particles and H-HCCI is set to 10, 30 and 60%, respectively, and the reinforced particles are mixed and stacked, the prepared sample has the best performance. The average nano-hardness of ZTA particles, the interface layer between ZTA particles and H-HCCI matrix, WC particles and H-HCCI matrix in the composites are 20.83, 19.08, 23.33 and 16.39 GPa, respectively. The Young's moduli of each component in the composites are 330.56, 289.41, 300.68 and 232.11 GPa, respectively. Based on the results of friction and wear experiments, the average wear depth of ZTA particles is 6.589 μm, the average wear depth of WC particles is 4.872 μm, and the average wear depth of H-HCCI matrix is 9.802 μm.Through performance testing, it was found that the hybrid reinforced composites showed excellent comprehensive properties. This paper provides theoretical support for multiphase reinforced composites, and proposes a new method for preparing ZTA particle reinforced metal matrix composites, which realizes the metallurgical interface bonding between ceramics and metals.
materials science, multidisciplinary