Abstract:Nanocrystalline magnesium aluminate spinel (MgAl 2 O 4 ) powders were synthesized in this study by employing a modified nitrate–citrate combustion route, in which the heat treatment was continuously performed by two separate processes. One process was in nitrogen during the carbonization of the precursors, and the other was subsequently in air. This can greatly decrease the heat release during the combustion process. X-ray diffraction and high-resolution transmission electron microscopy, differential scanning calorimetry, thermogravimetry, infrared spectroscopy, and inductively coupled plasma atomic emission spectrometer were utilized to reveal the reaction process and characterize the physical properties of precursors and powders. To achieve well-crystallized spinel powders with smallest possible and controllable crystallite sizes, the effect of carbonization in nitrogen on the calcined spinel powders was investigated in detail. The introduction of the inert atmosphere at the pre-calcination stage, with appropriate temperature and holding time, allowed ultra-fine, well-crystallized and size-controllable MgAl 2 O 4 powders with average crystallite sizes of 5–25 nm to be obtained. Despite the benefit from the pre-calcination in nitrogen, it was found that the stoichiometry of precursors can be compromised due to the loss of aluminum during the heat treatment in N 2 as the temperature was too high (>900 °C) with sufficient holding time. The mechanism of the carbothermal reduction was investigated in this study. Graphical Abstract By introducing inert atmosphere pre-calcination combustion, ultra-fine well-crystallized and crystalline size-controllable MgAl 2 O 4 spinel powders were thus obtained.

The Effect of Composition and Ph Value of Precursor Solution on Gel-Combustion Synthesis of MgO Nanocrystalline Powders

Effect of different fuel on MgO nanocrystalline powders prepared by low temperature combustion synthesis

The effect of pH value on sol-gel combustion synthesis of nanocrystalline LaMnO_3 powders

Synthesis of nanocrystilline ferrites by sol–gel combustion process: the influence of pH value of solution

SYNTHESIS OF NANOMETER MAGNESIA BY SOL- GEL METHOD

SYNTHESIS OF NANOCRYSTALLINE PARTICLES SnO2 BY GEL-COMBUSTION PROCESS

Synthesis of Nanocrystalline NiO/doped CeO2 Compound Powders Through Combustion of Citrate/nitrate Gel

The Effect of Citric Acid to Metal Nitrates Molar Ratio on Sol–gel Combustion Synthesis of Nanocrystalline LaMnO3 Powders

Effect of the citrate sol–gel synthesis on the formation of MgAl2O4 ultrafine powder

Study on Synthesis of Nanocrystalline Co3O4 Powders by Solution Combustion Technique and the Subsequent Heat Treatment Process

Preparation of Fine-powders by Auto-combustion of Citrate Gels

Mechanism of Auto Combustion Method in Synthesis of Nanocrystalline NiFe<SUB>2</SUB>O<SUB>4</SUB> Powders: Mechanism of Auto Combustion Method in Synthesis of Nanocrystalline NiFe<SUB>2</SUB>O<SUB>4</SUB> Powders

A Study on the Effect Factors of Sol-Gel Synthesis of Yttrium Aluminum Garnet Nanopowders

Mechanism of Auto Combustion Method in Synthesis of Nanocrystalline SiFe_2O_4 Powders

Preparation and characterization of NiCuZn ferrite nanocrystalline powders by auto-combustion of nitrate–citrate gels

Combustion synthesis and characterization of nanocrystalline CeO2-based powders via ethylene glycol–nitrate process

In-Situ Control of CaO-MgO-SiO2 Nanoparticles Synthesized by the Sol-Gel Method

Effect of MRCM on sol-gel synthesis of nano-grade NiO/Ce_(0.8)Gd_(0.2)O_(1.9) compound powders

Powder Synthesis and Characterization of Nanocrystalline CeO2 Via the Combustion Processes

Preparation and Characterization of MgO Nanopowder

Synthesis of ultra-fine and controllable size distribution nanocrystalline MgAl 2 O 4 powders and ascertainment of aluminum loss by introducing inert atmosphere pre-calcination during combustion