Abstract:A nanocrystalline Ce–Sm–oxide solid solution, with an excellent redox property and remarkable oxygen storage/release capacity, has been synthesized by means of a simple and highly practicable coprecipitation method. To understand the thermal and textural stability, the synthesized catalyst was subjected to calcination at various temperatures (773–1073 K). Physicochemical characterization was achieved using XRD, HRTEM, BET surface area, Raman, ICP-OES, XPS, TG-TDA, UV-vis DRS, TPR, and FTIR techniques, and the catalytic performance was evaluated for the oxidation of CO. Coprecipitation of Ce4+ and Sm3+ ions through ultra-high dilute solutions provided the single phase Ce0.6Sm0.4O2−δ solid solution in the nanoscale range, as confirmed by XRD and TEM studies. Raman studies revealed two types of lattice defects, namely, oxygen vacancies and MO8 complex defects due to disparity in the oxidation state and ionic radius of Sm3+ and Ce4+, respectively. Calculations made from XPS atomic ratios (Ce/Sm) and Raman band intensity ratios (AD1/AF2g) indicated migration of Sm from the bulk to the surface at elevated temperatures that caused a negative effect on the oxygen vacancy concentration. The doping of Sm3+ into the ceria lattice effectively enhanced the reduction behaviour of ceria by shifting the surface and bulk reduction to lower temperatures. Remarkably, Sm-incorporation showed an optimistic influence on the oxygen storage ability and CO oxidation efficiency of ceria attributed to profound lattice defects and enhanced bulk oxygen mobility. The salient features of physicochemical characterization versus catalytic CO oxidation efficiency of Ce–Sm–oxide solid solutions have been elaborated in this article.

Powder Synthesis and Characterization of Nanocrystalline CeO2 Via the Combustion Processes

Synthesis of Nanocrystalline Ce<sub>0.8</sub>Sm<sub>0.2</sub>O<sub>1.9</sub> by Citrate Gel Method

Estimating of Stearic Acid Dosage Using Self-Propagating Combustion Method in Synthesis of Nanocrystalline Ceo2 Powders

NANO-SCALE Sm0.15Gd0.05Ce0.8O1.9POWDER PREPARED BY COUPLING ROUTES OF SOL-GEL AND LOW TEMPERATURE SELF-PROPAGATING COMBUSTION

Citric–Nitrate Combustion Synthesis and Electrical Conductivity of the Sm3+ and Nd3+ Co‐Doped Ceria Electrolyte

Synthesis of Ce0.8Gd0.05y0.15O 1.9 nanopowders

Synthesis of Nanocrystalline Ce0.8sm0.2o1.9 by Citrate Gel Method

Synthesis of nanocrystalline Ce0.8Sm0.2O 1.9 by citrate gel method

Design Structure for Cepr Mixed Oxide Catalysts in Soot Combustion

Effect of fuels on the nanosized ceria powder by combustion method

Preparation and characterization of NiCuZn ferrite nanocrystalline powders by auto-combustion of nitrate–citrate gels

Synthesis of Ce<sub>0.8</sub>Gd<sub>0.05</sub>Y<sub>0.15</sub>O<sub>1.9</sub> Nanopowders

Synthesis and Characterization of BaCe0.8Y0.2O2.9 Nanopowder by Sol-Gel Auto-Ignited Method

Synthesis of nanocrystalline NiCuZn ferrite powders by sol–gel auto-combustion method

Synthesis and Characterization of Nanoscaled Cerium (IV) Oxide Via a Solid‐State Mechanochemical Method

Preparation of nano-sized CeO2 by mechanochemical reaction of cerium carbonate with sodium hydroxide

Preparation and Characterization of CeO<sub>2</sub> with Different Particle Sizes and Morphology

Synthesis and Characterization of BaCe<sub>0.8</sub>Y<sub>0.2</sub>O<sub>2.9</sub> Nanopowder by Sol-Gel Auto-Ignited Method

Nanocrystalline Ce1−xSmxO2−δ (x = 0.4) solid solutions: structural characterization versus CO oxidation

Synthesis of Nano-Crystalline CeO_2 Powders by DepositionMolten Salt Method

A Facile Combustion Synthesis of Ce0.8Sm0.2O1.9 Powders by in Situ Assembly of Polymer