Isovalent co-alloying contributes to considerable improvement in thermoelectric performance of BiSe bulks with weak anisotropy
Fu Li,Chen Liu,Mohammad Nisar,Jian Zhao,Chongbin Liang,Junze Zhang,Ziyuan Wang,Zhuanghao Zheng,Ping Fan,Xilin Wang,Zhen-Hua Ge,Yue-Xing Chen
DOI: https://doi.org/10.1016/j.jmat.2023.10.009
IF: 8.589
2023-11-10
Journal of Materiomics
Abstract:Highlights • BiSe based samples with high thermoelectric performance and weak anisotropy were successfully prepared. • Highest power factor of 12.8 μW/(cm·K 2 ) was achieved via isovalent co-doping of Sb and Te. • A BiSe based thermoelectric device with maximum energy conversion efficiency ∼ 4.0 % was firstly fabricated. BiSe with intrinsic low thermal conductivity has considered as a promising thermoelectric (TE) material at nearly room temperature. To improve its low thermoelectric figure of merit ( zT ), in this work, Sb and Te isovalent co-alloying was performed and significantly optimized its TE property with weakly anisotropic characteristic. After substituting Sb on Bi sites, the carrier concentration is suppressed by introduction of Sb Se site defects, which contributes to the increased absolute value of Seebeck coefficient (| S |). Further co-alloying Te on Se of the optimized composition Bi 0.7 Sb 0.3 Se, the carrier concentration increased without affecting the | S | due to the enhanced effective mass, which leads to a highest power factor of 12.8 μW/(cm·K 2 ) at 423 K. As a result, a maximum zT of ∼0.54 is achieved for Bi 0.7 Sb 0.3 Se 0.7 Te 0.3 along the pressing direction and the average zT ( zT ave ) (from 300 K to 623 K) are drastically improved from 0.24 for pristine BiSe sample to 0.45. Moreover, an energy conversion efficiency ∼4.0 % is achieved for a single leg TE device of Bi 0.7 Sb 0.3 Se 0.7 Te 0.3 when applied the temperature difference of 339 K, indicating the potential TE application. Graphical abstract Download : Download high-res image (331KB) Download : Download full-size image
materials science, multidisciplinary,chemistry, physical,physics, applied