Abstract:Bismuth telluride (Bi2Te3)-based alloys are widely used for thermoelectric cooling and power generation at low temperatures, and they are the only commercially available materials for thermoelectric applications below 500 K. The rhombohedral unit cell with a large c/a lattice constant ratio consisting of - Te-Bi-Te-Bi-Te- stacked layers inevitably brings about a large anisotropy in transport properties, which is why texturing is very important in polycrystalline Bi2Te3</sub alloys for maximum performance. In this report, p and n-type polycrystalline Bi2Te3</sub alloys were synthesized and hot-deformed to investigate the effects of texturing on thermoelectric properties. Hot deformation (HD) induces the strong alignment of (001) orientations along the compression direction, and a remarkable increase in the orientation factor F of (001) orientations is observed after HD in both p and n-type materials. All of the hot-deformed polycrystalline samples showed increased electrical conductivity (σ), power factor (PF), and thermal conductivity (k) in the in-plane (IP) direction, and vice versa in the out-of-plane (OOP) direction, which makes the IP direction of the hot-deformed bodies more favorable for module fabrication in terms of power factor, for both p and n-type Bi2Te3</sub-based alloys. However, due to the different degree of anisotropy of k and σ, the figures of merit (zT) were maximized in the OOP direction in the p-type materials after HD, whereas the zTs of the n-type materials were higher in the IP direction. This occurs because the anisotropy factor of electron conduction is higher than that of hole conduction, which more than offsets the advantage of the smaller k in the c-direction of n-type Bi2Te3</sub. The maximum zT of 1.33 (OOP) and 0.90 (IP) were obtained after HD from the p and n-type Bi2Te3 alloys, respectively, which were 9.3% and 18.4% higher than those of as-sintered materials.

Thermoelectric properties of hydrothermally synthesized and hot pressed n-type Bi2Te3 alloys with different contents of Te

Ultrasonic-assisted Hot Pressing of Bi2Te3-based Thermoelectric Materials

Hydrothermally Synthesized and Hot-Pressed Bi-2(Te,Se)(3) Thermoelectric Alloys

Thermoelectric Properties of Hydrothermal Synthesized Bi-Te-Se Alloys

Synthesis and Thermoelectric Properties of Bi2te3 Based Nanocomposites

Flower-like nanostructure and thermoelectric properties of hydrothermally synthesized La-containing Bi2Te3 based alloys

Thermoelectric and thermomechanical properties of the hot pressed polycrystalline Bi0.5Sb1.5Te3 alloys

Effect of Starting Powder Particle Size on the Thermoelectric Properties of Hot-Pressed Bi0.3Sb1.7Te3 Alloys

High-Performance p-Type Bi 2 Te 3 -Based Thermoelectric Materials Enabled via Regulating Bi-Te Ratio

Novel thermoelectric Bi2Te3 nanotubes and nanocapsules prepared by hydrothermal synthesis

Effect of Preparation Methods on Thermoelectric Properties of N-type Bi_2Te_(2.4)Se_(0.6) Bulk Alloys

Enhanced Thermoelectric Properties Obtained by Compositional Optimization in P -Type Bi X Sb 2− X Te 3 Fabricated by Mechanical Alloying and Spark Plasma Sintering

Improved Thermoelectric Properties of Bi2Te3−xSexalloys by Melt Spinning and Resistance Pressing Sintering

Structures and Electric Properties of Bi2Te3 Based Alloys Prepared by Solvothermal Synthesis

Analysis of Thermoelectric Properties of Hot-deformed Bismuth Telluride Sintered Materials

Development of Nanostructured Bi2Te3 with High Thermoelectric Performance by Scalable Synthesis and Microstructure Manipulations

Enhanced Thermoelectric and Mechanical Properties of p-type Bi0.5Sb1.5Te3 Bulk Alloys by Composite Electroless Plating with Ni&Cu

Optimized Thermoelectric Properties of Bi0.48Sb1.52Te3 Through AgCuTe Doping for Low-Grade Heat Harvesting.

Solvothermal synthesis and thermoelectric properties of lanthanum contained Bi–Te and Bi–Se–Te alloys

Thermoelectric Performance Enhancement in N -Type Bi 2 (tese) 3 Alloys Owing to Nanoscale Inhomogeneity Combined with a Spark Plasma-Textured Microstructure

Broad-Temperature Thermoelectric Figure of Merit Enhancement in Unconventional n-Type Bi 2 Te 2.3 Se 0.7 Alloys