Abstract:In this paper, the Pulse-Reverse Current (PRC) electroplating technique was utilized to deposit Ni-Cu alloy coatings on the surface of Nd-Fe-B magnets. Compared with the Ni coating, the corrosion resistance of the Ni-Cu alloy coating has been significantly improved, with the corrosion potential Ecorr and the corrosion current density Icorr of -246 mV and 0.9 μA·cm-2, respectively. The results show that alloying can effectively prolong the incubation period of pitting nucleation and improve the self-healing ability of coating. The structure and microstructure of the coating show that the surface of the Ni-Cu coating is flat and the grains preferentially grow along the (111) close-packed surface, which also makes the coating have higher densification and significantly reduces the number of self-corrosion sites and corrosion tendency of the coating. The lower binding energy Cu2O produced by Ni-Cu coatings at the initial corrosion stage can reduce the formation of metal cation holes and prolong the incubation period of pitting corrosion. After pitting formation, the corrosion products Cu2O and Cu2(OH)3Cl of Cu in the pitting hole have a certain hindrance to corrosion and are conducive to promoting passive reconstruction, which is an important reason for the Ni-Cu alloy coating shows higher self-healing ability and higher corrosion resistance.

Corrosion Behavior of Spark Plasma Sintering NdFeB Magnets

Corrosion behavior of Nd-Fe-B sintered magnets at remanence state

Study Magnetic Properties and Corrosion Resistance of Sintered NdFeBAlDyNb Magnets

EFFECTS OF ULTRASONIC ELECTROLESS Ni- P PLATING ON THE CORROSION RESISTANCE OF SINTERED NdFeB MAGNETS

Corrosion Protection of Nd-Fe-B Sintered Magnets by Aluminum Coating

Effect of electroless deposition on the corrosion resistance property for NdFeB permanent magnets with surface coating of Ni-P alloy

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

Corrosion Behavior of Sintered NdFeB Magnets Coated with Ni Coatings Deposited by Ion Beam Sputtering

A design of sintered Nd-Fe-B magnet exhibiting superior corrosion resistance based on the metallurgical behavior of Ni and Cr

Corrosion Resistance of Nd–Fe–B Sintered Magnets with Intergranular Addition of Cu60Zn40 Powders

Corrosion Protection of Nd–Fe–B Magnets by Silanization

Towards Peculiar Corrosion Behavior of Multi-Main-phase Nd-Ce-Y-Fe-B Permanent Material with Heterogeneous Microstructure

Corrosion mechanism of Ni deposits on magnets by pulse current electro-deposition

Electrochemical Corrosion Behavior of Hot-Deformed NdFeB Magnet with Different Content of Nano-Tic

Effects of Nd3+ on adhesion and corrosion resistance of electroless Ni-P coating on sintered Nd-Fe-B magnets

Electroless Ni-Co-P Coatings on Sintered Nd-Fe-B Magnets with Improved Corrosion Resistance

Amorphous Al–Mn Coating on NdFeB Magnets: Electrodeposition from AlCl3–EMIC–MnCl2 Ionic Liquid and Its Corrosion Behavior

Anti-corrosion performance of Si-surface-alloying NdFeB magnets obtained with magnetron sputtering and thermal diffusion

Corrosion behavior and strengthening mechanism of Ni-Cu alloy coating on Nd-Fe-B magnets

Fabrication of Epoxy Composite Coatings with Micro-Nano Structure for Corrosion Resistance of Sintered NdFeB

Fabrication and Properties of Micro-arc Oxidation Coatings on Sintered NdFeB Permanent Magnets