The effects of MoO3 addition on microwave dielectric properties of Bi6B10O24 ceramics for ULTCC applications
Xiaoyan Xia,Ying Dai,Siqi Sun,Wen Chen,Feng Zhang,Xinmei Pei
DOI: https://doi.org/10.1007/s10854-024-12342-9
2024-03-23
Journal of Materials Science Materials in Electronics
Abstract:Microwave ceramic with low‐sintering temperature is one of the most significant classes of materials to realize the multifunction and miniaturization of portable devices. In this paper, Bi 6 B 10 O 24 ceramics using the solid-state reaction method are prepared with MoO 3 addition, to achieve both low-temperature sintering and excellent microwave dielectric properties. It is demonstrated that MoO 3 diffuses into the lattice of Bi 6 B 10 O 24 to form a solid solution. The higher quality factor (Q × f ) of the ceramic is successfully obtained and the temperature coefficient of resonant frequency (τ f ) is adjusted to near zero at the same time without much change in the dielectric constant ( ε r ) due to the Mo 6+ incorporation. Compared to Bi 6 B 10 O 24 ceramics without addition, the optimum properties of ε r = 13.9, Q × f = 37,000 GHz, τ f = − 20 ppm/°C are achieved for Bi 6 B 10 O 24 ceramics containing 19 mol% MoO 3 . The ceramics are potential candidates for ultra-low temperature co-fired ceramics (ULTCC) applications in wireless communication systems.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied