Abstract:Self assembled AlN nanowires (NWs) are grown by plasma assisted molecular beam epitaxy (PAMBE) on SiO2 / Si (111) substrates. Using a combination of in-situ reflective high energy electron diffraction and ex situ X ray diffraction (XRD), we show that the NWs grow nearly strain free, preferentially perpendicular to the amorphous SiO2 interlayer and without epitaxial relationship to Si(111) substrate, as expected. Scanning electron microscopy investigation reveals significant NWs coalescence, which results in their progressively increasing diameter and formation of columnar structures with non hexagonal cross section. Making use of scanning transmission electron microscopy (STEM), the NWs initial diameters are found in the 20 to 30 nm range. In addition, the formation of a thin (30 nm) polycrystalline AlN layer is observed on the substrate surface. Regarding the structural quality of the AlN NWs, STEM measurements reveal the formation of extended columnar regions, which grow with a virtually perfect metal-polarity wurtzite arrangement and with extended defects only sporadically observed. Combination of STEM and electron energy loss spectroscopy (EELS) reveals the formation of continuous aluminum oxide (1 to 2 nm) on the NW surface. Low temperature photoluminescence measurements reveal a single near band edge (NBE) emission peak, positioned at 6.03 eV (at 2 K), a value consistent with nearly zero NW strain evidenced by XRD and in agreement with the values obtained on AlN bulk layers synthesized by other growth techniques. The significant full width at half maximum of NBE emission, found at 20 meV (at 2 K), suggests that free and bound excitons are mixed together within this single emission band.

Optical Properties of Highly Ordered Aln Nanowire Arrays Grown on Sapphire Substrate

Raman Spectrum of Array-Ordered Crystalline Silicon Nanowires

Synthesis and Raman Spectra of Si-Nanowires

Crystallization and Raman Shift of Array-Orderly Silicon Nanowires after Annealing at High Temperature

Synthesis and Optical Property of High Purity Aln Nanowires

Controlled synthesis of ultra-long AlN nanowires in different densities and in situ investigation of the physical properties of an individual AlN nanowire.

Array-orderly single crystalline silicon nano-wires

Optical Properties of Mono-Dispersed AlGaN Nanowires in the Single-Prong Growth Mechanism

Structural and optical properties of self-assembled AlN nanowires grown on SiO2/Si substrates by molecular beam epitaxy

Ordered Arrays of High-Quality Single-Crystalline Α-Si3n4 Nanowires: Synthesis, Properties and Applications

P2&#x2013;24: Controlled Growth of Ultra-Long AlN Nanowire Arrays in Different Density and Investigation of Their Emission Behaviors

Optical Properties of Quasi-Ordered 112̅2 AlGaN Multi-Quantum-well Nanorod Arrays

Optical properties of quasi-ordered 11 2 ̅ 2 AlGaN multi-quantum-well nanorod arrays

Structural And Raman Properties Of Compositionally Tunable Alxga1-Xn (0.66 <= X <= 1) Nanowires

Fabrication and Photoluminescence of Ordered GaN Nanowire Arrays

Single-crystalline Alpha Silicon–nitride Nanowires: Large-scale Synthesis, Characterization, and Optic Properties

Large-scale AlN Nanowires Synthesized by Direct Sublimation Method

Ordered Semiconductor CdO Nanowire Arrays: Synthesising by One-Step Low-Temperature Electrodeposition and Optical Properties

Structural and Electronic Properties of [0001] AlN Nanowires: A First-Principles Study

High Efficiency Ultraviolet Emission from AlxGa1−xN Core-Shell Nanowire Heterostructures Grown on Si (111) by Molecular Beam Epitaxy

Formation and photoluminescence properties of AlN nanowires