Abstract:For joining, the same SiC nano-powder and sintering additive with NITE processing to fabricate SiC were used. Silicon carbide or SiC/SiC plates were joined by hot-pressing at 1700-1900 °C for 1 hour under 20 MPa. The joined bars were evaluated by tensile test and asymmetric four point flexural test. For the coating, W is used considering the application. Starting materials were both fme powders and by lay-up two zones of powders (slurry) followed by hot pressing, two layers of W and SiC were produced with strong bonding. The joint thickness was controlled to approximately 10 μm. The tensile strength for the joint of monolithic SiC was approximately 40 MPa with 40% porosity at the interface. The shear strength of the joint of monolithic SiC could not be obtained, since the crack at joint propagated into the substrate, but it was more than 90 MPa. After improving the technique, the dense joint was formed and then, the tensile strength increased to more than 250 MPa. For W coated SiC, SiC, W and their interface reaction layers can be controlled to make acceptable bonding by optimizing the materials used and process condition. Using the optimized condition, W coated SiC/SiC composites were developed, although the optimization of processing for the composites is still required.

Effect of nickel nanopowders addition on joining property of silicon carbide to itself by polysilazane

Joining of pressureless sintered SiC using polysiloxane SR355 with active additive Ni nanopowder

Joining of SiC by high temperature brazing with Ni-51Cr filler

Microstructure and mechanical properties of SiC/SiC joints reinforced by in-situ growth SiC nanowires

Joining of Recrystallized SiC Ceramic Using Ni-Cr-Nb Powders as Filler

Joining of SiC ceramics by combining NITE-SiC interlayer and its thickness control

Improved the Mechanical Properties of SiCf/SiC-GH536 Joints by In-Situ Introducing Better Toughness MoNiSi Phase to the Brazing Seam

Study on crosslinking of polymers and joining mechanism of SiC ceramic

Interfacial reaction mechanism of SiC joints joined by pure nickel foil

Investigations of the effect of Si addition on graphite elimination and the oxidation behavior of SiC joint using Inconel 625 powder filler

Improving the Brazing of SiC Ceramic by Nano-Si3n4 Reinforced BNi-2 Composite Filler Prepared by High-Shear Processing

Low-temperature joining of SiC ceramics by NITE phase using CaO-Al2O3-MgO-SiO2 glass as an additive combined with surface oxidation

Wettability and Joining of SiC by Sn-Ti: Microstructure and Mechanical Properties

Joining silicon nitride ceramics with ZrSi2-SiC composite filler by spark plasma sintering

The Formation Process and Strengthening Mechanism of SiC Nanowires in a Carbon-Coated Porous BN/Si3N4 Ceramic Joint

Effect of SiC Nanowires on the Thermal Shock Resistance of Joint Between Carbon/carbon Composites and Li2O–Al2O3–SiO2 Glass Ceramics

Joining of SiC Ceramic by Using the Liquid Polyvinylphenylsiloxane

Semisolid Compression Brazing of Al50Si Alloy Using Zn-Al-Cu Filler Metal Assisted by SiC Particles

Joining SiC ceramics with ZrSi2–SiC filler at low temperatures

Development of Joining and Coating Technique for SiC and SiC/SiC Composites Utilizing Nite Processing

Recent advances in joining of SiC-based materials (monolithic SiC and SiCf/SiC composites): Joining processes, joint strength, and interfacial behavior