Abstract:SiC/SiC composites, prepared by reactive melt infiltration (RMI), exhibit exceptional properties. However, the presence of residual Si in the composite matrix can significantly compromise their high-temperature mechanical properties. Addressing the issue of high-content residual Si aggregation remains a crucial focus of research in order to fully unlock the application potential of SiC/SiC composites prepared by RMI. In this work, a special porous carbon (C g ) is successfully synthesized and introduced into the porous 2D SiC/SiC composites prepared by CVI. The unique pore structure of the SiC/SiC-C g is thoroughly analyzed, along with its liquid Si infiltration process. The difference in coefficient of thermal expansion (CTE) between SiC and C g can cause thermal stress, which can destory the C g structure. Consequently, the C particles detach from the C g skeleton and react with liquid Si to create SiC. This process effectively separates residual Si and helps alleviate the negative effects of residual Si aggregation. The microstructure and phase distribution of SiC/SiC composites obtained by liquid Si infiltrating different C structures are investigated and compared, and it demonstrates the positive effect of C g on the uniform phase distribution of matrix in the composites. The as-received SiC/SiC composites possess a density of 2.94 g/cm 3 with open porosity of 1.23%, and a flexural strength of 808.7±10.2MPa, a fracture toughness of 25.5±1.8MPa·m 1/2 , a tensile strength of 317.4±12.4MPa and a proportional ultimate stress of 157.33±4.1MPa. Acoustic emission (AE) and digital image correlation (DIC) technology are used to study the special mechanical behavior of composites.

Influence factor of MoSi2-SiC composites synthesised by reactive infiltration processing

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

MoSi_2/SiC COMPOSITE PREPARED BY USING REACTION - MELTING INFILTRATION SINTERING

Influence of the Porosity of C/C on the Characterization of C/C-Sic Composites Prepared by Reactive Melt Infiltration Method

Influence factors of C/C–SiC dual matrix composites prepared by reactive melt infiltration

Effect of infiltration time on the microstructure and mechanical properties of C/C-SiC composite prepared by Si‐Zr10 alloyed melt infiltration

Influence of Process on the Bending Strength of SiC_f/Si-O-C Composite

Microstructures Andmechanical Properties of Hot-Pressed MoSi 2-Matrix Composites Reinforced with SiC and Si 3 N 4 Particles

A novel porous carbon synthesized to serve in the preparation of highly dense and high-strength SiC/SiC by reactive melt infiltration

Elevated temperature strengthening of synthesized in situ MoSi2-SiC composite

MoSi2 Composites Reinforced by SiC Whiskers and Si3N4 Particles

Microstructure and mechanical properties of SiCp/MoSi2 composites prepared by in situ synthesis and hot-pressing

Microstructure, Interfacial and Mechanical Properties of SiC Interphase Modified C/C-SiC Composites Prepared by Reactive Melt Infiltration

Improving Mechanical Properties of SiCw/SiC Composite by Phase Content Optimization Via Reactive Melt Infiltration

THE MICROSTRUCTURE AND MECHANICAL PROPERTY OF SiCp/MoSi2 BY IN-SITU REACTION AND HOT PRESS

The Microstructure and Mechanical Property of Mo(Si, Al)2-SiC Composite Prepared by Infiltrating Melt Aluminum

Microstructure and flexural strength of C/HfC-ZrC-SiC composites prepared by reactive melt infiltration method

Influence of Adding Al on the Microstructure and Mechanical Properties of C/C-SiC Composites Fabricated by MSI

Effect of C/C Preform Density on Microstructure and Mechanical Properties of C/C–SiC Composites Prepared by Alloyed Reactive Melt Infiltration

Effect of chemical vapor infiltration on the flexural properties of C/C-SiC composites prepared by the precursor infiltration pyrolysis method

Effect of SiC content on the mechanical behaviour of a three-dimensional needled C/SiC composite