Preparation and characterization of BaMgAl10O17:Eu phosphor coated with MgF2 by sol-gel process

Feng Li,Yuhua Wang,李峰,王育华

IF: 3.752

2005-01-01

Transactions of Nonferrous Metals Society of China

Abstract:In order to prevent BaMgAl10O17 : Eu (BAM) phosphor from thermal degradation, MgF2-coatings on the surface of BAM were prepared by a sol-gel process. The coatings were characterized by X-ray photoelectron spectroscopy and scanning electron microscopy. The results indicate that BAM is successfully coated with homogenous, close MgF2 coatings. The photoluminescence and anti-thermal degradation properties of coated BAM were investigated under 254 and 147 nm excitations. The optimum anti-thermal degradation properties are obtained at the mass ratio of MgF2 to BAM 0.2% under 254 nm excitation and 0.5% under 147 ran excitation, respectively. It is considered that trace MgO formed after baked would cause different optimum coating thicknesses under 254 and 147 nm excitations.