Abstract:Highly efficient blue-emitting NaBa4(AlB4O9)(2)X-3 (X = Cl, Br): Eu2+ phosphors (NBAC: Eu2+ and NBAB: Eu2+) were prepared by solid-state reaction. Two different crystallographic cation sites of Eu2+ ion occupancy were confirmed by Rietveld structural refinement, photoluminescence spectroscopy and measurement of fluorescence decay lifetimes. The NBAC: Eu2+ and NBAB: Eu2+ phosphors exhibited broad excitation ranging from 250 to 420 nm, both of which overlapped well with the emission of n-UV LED chips. Under 365 nm excitation, intense asymmetric blue emission bands were obtained for NBAC: Eu2+ and NBAB: Eu2+, peaking around 429 and 437 nm, respectively. The optimal Eu2+ doping concentration in both NBAC: xEu(2+) and NBAB: xEu(2+) was determined to be the same (10 mol%). The concentration quenching mechanism turned out to be electric dipole-dipole interactions. The NBAB: 0.1Eu(2+) and NBAC: 0.1Eu(2+) phosphors presented superior blue-emitting properties to the commercially available BAM: Eu2+ blue phosphor. The optimized NBAB: 0.1Eu(2+) and NBAC: 0.1Eu(2+) exhibited high external quantum efficiencies of 98.7% and 74.7% of the commercially available compound BaMgAl10O17: Eu2+ (BAM: Eu2+), respectively, while the NBAB: 0.1Eu(2+) phosphor demonstrated a very narrow band (FWHM <= 33 nm) and an ultra-high color purity of 99.58%. These results suggest that NBAB: Eu2+ and NBAC: Eu2+ can serve as promising blue-emitting candidates for n-UV pumped white LEDs.

Preparation and Luminescent Properties of BAM Blue Phosphor Forpdp and CCFL

BaMgAl10O17:Eu2+ Mn2+ Blue-Green Phosphor for White Light Emitting Diodes

Luminescence of Ba 0.85 MgAl 10 O 16.94 :Eu 2+ 0.09 with Different Fluxes

Luminescence of Ba0.85MgAl10O16.94:Eu 0.09 2+ with different fluxes

Luminescence of Ba0.85MgAl10O16.94 : EU0.092+ with different fluxes

Luminescence of Bax−0.05MgAl10O16+x: Eu2+0.05 with Different Ba2+ Content

Synthesis and luminous characteristics of Ba 3 CaSi 2-x Al x O 8 :Eu, Mn phosphor for white LED

Synthesis and luminous characteristics of Ba2MgSi2-xAlxO7: 0.1Eu2+, 0.1Mn2+ phosphor for WLED

Microstructure and Luminescence of Surface-Coated Nano-Bamgal10o17:Eu2+ Blue Phosphor

Structure and Luminescence Properties of Bi3+ Activated Ca12Al14O32Cl2 Phosphors

Preperation and Photoluminescent Properties of Ca2AlSi3O2N5:Sm3+ Phosphor

Energy Transfer and Photoluminescence of BaMgAl10O17 Co-Doped with Eu2+ and Mn2+

Preparation and Luminescence Properties of Al18B4O33:Eu,Tb Phosphor

Preparation And Luminescence Properties Of The New Long Phosphorescent Phosphors Ba1-Xcaxal2o4 : Eu2+, Dy3+

Emission of BaMgAl_(10)O_(17):Eu~(2+) with High Concentration of Activator

Luminescent properties of SrMgAl10 O17∶Eu2+,Mn2+ high-efficiency phosphor prepared via the sol-gel combustion method

Preparation of CaYAl3O7:Ce3+, Tb3+ Blue-Green Phosphors by Sol-Gel Process

Eu2+-Doped NaBa4(AlB4O9)2X3 (X = Cl, Br) Phosphors with Intense Two-Center Blue Emission and High Color Purity for N-Uv Pumped White Light-Emitting Diodes

Preparation and cathodoluminescence characteristics of rare earth activated BaAl2O4 phosphors

Phosphor of 2(Sr,ba)o-0.16B2o3-0.84p2o5:Eu2+ for UV-LED

Intense photoluminescence and mechanoluminescence of novel BaLaAl3O7:xEu3+ red nanophosphors