TiB2 Reinforced AlFeVSi Alloy by Rapid-Solidified Powder Metallurgy

LI Qing-yong,WANG Ri-chu,WEI Sheng-ming,LI Wen-xian,HUANG Bai-yun
DOI: https://doi.org/10.3321/j.issn:1004-0609.2005.04.024
2005-01-01
Abstract:The samples of Al-8.5Fe-1.3V-1.7Si aluminium alloy with and without TiB_2 particles reinforcement were prepared by rapid-solidified powder metallurgy. The microstructure and fractography of the samples were studied by means of the optical microscope and scanning electron microscope, and the mechanical properties were analyzed by tensile experiment. The results show that TiB_2 particles can be added to the AlFeVSi aluminium alloy and restrains the form of equilibrium phase Al_(13)Fe_4 . The crystal grain is refined and the mechanical properties are improved. The samples with TiB_2 particles which are smaller than 74μm show the best mechanical properties.The fracture strength, yield strength and elongation reach to 454.1MPa, 407.8MPa, 7.7% respectively at room temperature. The elevated temperature strength and elongation stay stable over 210MPa and 7.7% at 350℃.
What problem does this paper attempt to address?