Abstract:YEuxBa2Cu3.6O7−δ (x = 0, 0.1, 0.3, 0.5) thin films were prepared on buffered substrates by trifluoroacetate metal organic deposition (TFA-MOD). The europium-doped film showed better out- and in-plane texture than the pure YBa2Cu3.6O7−δ thin film and special topography. In the meantime, the superconducting transition temperature T c was improved with the increase of europium content and spanned a small range when x= 0.5 doping levels. Besides, the J c value was obviously enhanced with europium addition, and YEu0.3Ba2Cu3.6O7−δ showed the best superconducting properties under self-field. Furthermore, the J c value was obviously improved under magnetic field, and the enhanced flux-pinning properties was also observed in europium-substituted samples which may be attributed to the good grain connections and the effective flux pinning centers introduced by europium addition. The thickness of prepared film samples were approximately 400 nm. The structure of samples were characterized by x-ray diffraction (XRD), Raman spectrum was used to investigate the crystallization and growth orientation, and the surface morphology of films were got by field-emission scanning electronic microscopy (FE-SEM). Moreover, energydispersive spectroscopy (EDS) was utilized to determine element composition. Spatial distribution of J c of the film was obtained by mapping analysis of inductive measurement at 77 K. And the superconducting properties under magnetic fields were measured by magnetic property measurement system with a SQUID magnetometer.

Characteristics of Y1-Xcaxba2cu3o7-Delta Thin Films Grown by Dc Magnetron Sputtering

Superconducting Characteristics and Epitaxial-Growth Analyses of YBa2Cu3O7−x Thin Films by Direct-Current Magnetron Sputtering

Superconducting properties and structural perfection of epitaxial YBa 2 Cu 3 O 7- x thin films

Epitaxial Growth of Differently Doped (caxla1−x)(ba1.75−xla0.25+x)cu3oythin Films Byin Situdc Magnetron Sputtering

Preparation of YBa2Cu3O7−δ Thin Films by Magnetron Sputtering with I N S I T U Plasma Oxidation

Batch Production of Large-Area Double-Sided Yba2cu3o7-Delta Thin Films by Dc Magnetron Sputtering

CaCu33Ti44O1212 Films Prepared by Magnetron S Puttering

Morphology and Structure of La1.85Sr0.15CuO4 + Δ Thin Films Deposited on (100) SrTiO3 Substrates by Dc Magnetron Sputtering

Cacu3ti4o12 Films Prepared by Magnetron Sputtering

Influence of Deposition Temperature on the Superconductivity of Y1?x HoxBa2Cu3O7 ??films Produced by Dc-Magnetron Sputtering

Preparation of Electron-Doped La2−xCexCuO4±δ Thin Films with Various Ce Doping by Dc Magnetron Sputtering

Studies of high temperature superconducting thin films by transmission electron microscopy

Growth and Annealing of La1.85Sr0.15CuO4+δthin Films on SrTiO3substrates

Epitaxial YBa/sub 2/cu/sub 3/o/sub 7- Delta / Thin Films on LaMgAl/sub 11/o/sub 19/: New Substrates with Low Dielectric Losses

Surface Structure and Transport Properties of Yba2cu3o7-Delta Using La2/3ca1/3mno3 As Buffer

STUDY OF THE PREPARATION OF HIGH Tc SUPERCONDUCTING YBCO THIN FILMS BY A PLASMA-ASSISTED MOCVD PROCESS

The Characterization of Superconducting Tungsten Thin Films Deposited by DC Magnetron Sputtering

Enhancing superconductivity of ultrathin YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub> films by capping non-superconducting oxides*

Surface Structure and Transport Properties of <font>YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub></font> Using <font>La<sub>2/3</sub>Ca<sub>1/3</sub>MnO<sub>3</sub></font> as Buffer

Preparation of Yba2cu3o7-X Superconducting Thin-Films over Large Area Substrates

Microstructures Property and Improved J C of Eu-Doped YBa2Cu3.6O7−δ Thin Films by Trifluoroacetate Metal Organic Deposition Process