Abstract:Low power nanosecond laser irradiation has potential applications in surface processing of metallic glasses (MGs). However, the response of MGs to a relatively low power intensity (1011 W/m2) has not been investigated. In this study, surface microstructures and characteristics of Zr-based MG after low power nanosecond laser irradiation were studied. Micro-cracks with depth in nanoscale and width in microscale were observed on the irradiated MG surface. The effects of laser parameters on the formation and evolution of micro-cracks were further investigated, and surface characteristics were characterized by using X-ray diffraction (XRD) and energy dispersive X-ray spectroscopy (EDS). The results showed that under the peak laser power intensity of 2.3 × 1011 W/m2, when increasing the scanning speed from 1 to 5 mm/s, the maximum width of micro-cracks reduced from 3 μm to be less than 1 μm; further increasing to 10 mm/s, no micro-cracks appeared. When increasing the laser power intensity, the micro-groove structure would be formed with pileup around it and line cracks, open cracks and laser pulse tracks on it. During multi-line laser scanning, the pulse overlap rate also affected the formation and distribution of micro-cracks. At last, the formation mechanism of micro-cracks was discussed. These results would be meaningful for understanding the laser-MG interaction as well as guiding the selection of laser parameters for various applications.

Relationship Between Micro-Structure And Laser Damage Threshold Of Nano-Zro2 Films

Studies on Micro-Structure of Nano-ZrO2 Films

Researches on Laser Damage Resistance of Optical Films

Laser-induced damage threshold of ZrO2 thin films prepared at different oxygen partial pressures by electron-beam evaporation

Experimental research of laser-induced damage of the monolayer ZrO2 PVD and sol–gel films

Comparison of Laser-Induced Damage of Monolayer ZrO2 Films Preparated by PVD and Sol-Gel Methods

Modification and Laser-Damage Resistance of Zirconia Thin Films

Contrast Study of Laser-induced Damage of Monolayer SiO2 and ZrO2 Films

Effect of ZnO Nanostructures on 2-Dimensional Random Lasing Properties

Comparative studies of laser-induced damage of several single-layer optical films

Laser-conditioning Mechanism of ZrO2/SiO2 HR Films with Fitting Damage Probability Curves of Laser-Induced Damage

Influence of O2 Partial Pressure on the Micro-structure of ZrO2 Thin Films by Electron Beam Evaporation

Study of Laser-Irradiated Thin Films

Influence of Porosity on Laser Damage Threshold of Sol–gel ZrO2 and SiO2 Monolayer Films

Laser induced micro-cracking of Zr-based metallic glass using 1011 W/m2 nano-pulses

The Effect of Laser Irradiation on Zno Thin Films

Preparation of Sol–gel ZrO2–SiO2 Highly Reflective Multilayer Films and Laser-Induced Damage Threshold Characteristic

Femtosecond Laser-Induced Damage and Ultrafast Dynamics in Highs Reflection Coating

Effect of porosity on the laser induced damage threshold of sol-gel SiO2 and ZrO2 single layer films

Laser damage mechanisms of a variable refractivity thin film consists of non-quarter-wavelength film layers

Sol-Gel Processing of Zirconia Coating for HR Mirrors with High Laser Damage Threshold