Preparation and Corrosion Resistance of γ-aminopropyltriethoxysilane-TiO2-GO/Waterborne Polyurethane Coating
Xia Wang,Xiong Li,Ling-long Xu,Qiao Zhang,Yue Gu,
DOI: https://doi.org/10.20964/2020.11.44
IF: 1.541
2020-11-01
International Journal of Electrochemical Science
Abstract:In this paper, γ-aminopropyltriethoxysilane-TiO2-GO (KTG) composite particles were prepared using γ-aminopropyltriethoxysilane (KH550) by depositing nano-TiO2 on graphene oxide (GO) substrate. The KTG/waterborne polyurethane (WPU) composite coating was prepared by blending KTG with WPU. Fourier transform infrared spectroscopy (FTIR), x-ray diffraction (XRD), and scanning electron microscope (SEM) were employed to characterize the composition and structure of the GO before and after the modification, while the water resistance, thermal stability and corrosion resistance of the composite coating were examined via water absorption test, contact angle test, thermogravimetric analysis (TGA), and electrochemical impedance spectroscopy (EIS). The results showed that nano-TiO2 was successfully deposited on the GO surface. The incorporation of KTG composite particles reasonably improved the water resistance, thermal stability and corrosion resistance of the WPU coating. Optimum water resistance of the composite coating with 0.9% KTG incorporation, 1.3% water absorption rate reduction relative to the pure WPU coating, and 283 to 300°C increment in thermal decomposition temperature were achieved. Moreover, the corrosion resistance of the composite coating was significantly improved. Furthermore, a value of 7.89×106 Ω·cm2 coating resistance of the composite coating, 2.56×10-9 A·cm-2 corrosion current density, and 99.81% corrosion inhibition efficiency can attained.
electrochemistry