Effect of Bi2O3 on the Phase Transformation and Properties of Glass Ceramics

陈国华,刘心宇

DOI: https://doi.org/10.3969/j.issn.1005-0299.2004.05.014

IF: 1.8

2004-01-01

Materials Science and Technology

Abstract:Cordierite-based glass ceramics containing different amounts of Bi2O3 were prepared by the sintering method. The effect of Bi2O3 on the phase transformation, sintering and property of cordierite-based glass ceramics was studied using XRD, SEM,thermal dilatometer and impedance analyzer. The results showed that the addition of Bi2O3 could lower the phase transformation temperature from u-to a- cordierite and enhance the densification of cordierite-based glass. The dielectric constant and the flexural strength of samples increased with the addition of Bi2O3 in a similar way as that of the density. With the addition of 5wt% Bi2O3, the dissipation factor of the sample showed the lowest value (10-3). The thermal expansion coefficients of the samples with different amounts of Bi2O3 exhibit the characteristic of linearity.