Abstract:The preparation of aluminum-containing silicon carbide,SiC(Al),fibers by using polyaluminocarbosilane(PACS) and polycarbosilane(PCS) blends as precursors was investigated.The solubility parameter of PACS was determined to be 18 MPa 1/2 by dissolving PACS in solvents with different solubility parameters.It was very close to the solubility parameter of PCS(18.4 MPa 1/2),indicating the possible compatibility of PACS and PCS.After PACS and PCS both were dissolved in xylene,a translucent yellow blend of PACS and PCS,B-PACS,was obtained by distillation.The composition and structure of B-PACS,PACS and PCS were characterized by chemical analysis,GPC and FTIR.It was found that B-PACS with desirable Al contents could be obtained by adjusting the ratio of PACS(Al content 1.25 wt%) and PCS.The Si—H bond content can be indicated by A_ 2100 cm-1 /A_ 1250 cm-1,where A_ 2100 cm-1,A_ 1250 cm-1 are the absorbance of Si—H bonds at 2100 cm-1 and CH_3 bonds at 1250 cm-1,respectively.The FTIR results showed that the Si—H bond content of B-PACS was higher than that of PACS,while their Al contents were the same.PCS with a higher Si-H content might be responsible for the higher Si—H content of B-PACS.GPC results showed that B-PACS had a high molecular weight fraction as compared with PACS of the same Al content.The apparent activation energy of flow for B-PACS and PACS(Al content 0.6 wt%) was determined by the relationship between temperature and melt viscosity.They were 200 kJ/mol and 255 kJ/mol,respectively.The better spinnability of B-PACS was approved by spinning experiments,and finer B-PACS green fibers were obtained.The tensile strength of Si-Al-C-O fibers from PACS and B-PACS were 2.0 GPa and 2.4 GPa,respectively.The higher strength of Si-Al-C-O fibers from B-PACS might be related with the finer diameter of the green fibers and the high molecular weight fraction in B-PACS.The SiC(Al) fibers derived by curing PACS and B-PACS green fibers at 1800℃ in Ar were compact and smooth,while the SiC fibers derived from PCS had pores and defects.The introduction of Al into SiC fibers may reduce the growth of SiC crystallites in fibers.The average sizes of SiC crystallites in fibers derived from B-PACS,PACS and PCS were 8.5 nm,9.6 nm and 14 nm,respectively.

A Near-Stoichiometric Sic-Based Fibre Obtained from A Polyaluminocarbosilane Precursor

Fabrication and Properties of Aluminum-Containing Silicon Carbide Fibres

Characterization and Microstructural Evolution of SiC(OAl) Fibers to SiC(Al) Fibers Derived from Aluminum-Containing Polycarbosilane

The Preparation and Properties of High Temperature Resistant Sic(Al) Fibers

Continuous Si–C–O–Al Fiber Derived from Aluminum-Containing Polycarbosilane Precursor

Continuous Sic(Oal) Fiber from Polymer Precursor

Preparation and properties of continuous Al-containing silicon carbide fibers

HIGH TEMPERATURE RESISTANCE SiC(Al) FIBERS

Composition and Structure of Polymer-derived Aluminium-containing SiC Fibers

PREPARATION OF ALUMINUM-CONTAINING SILICON CARBIDE FIBER SINTERED AT HIGH TEMPERATURE

Structural Evolution and Associated Properties on Conversion from Si-C-O-Al Ceramic Fibers to Si-C-Al Fibers by Sintering

STUDY OF HIGH TEMPERATURE RESISTANT SiC(Al) FIBERS PRECURSOR-POLYALUMINOCARBOSILANE FIBERS

HIGH-TEMPERATURE RESISTANCE PROPERTIES OF SILICON CARBIDE FIBERS CONTAINING ALUMINUM

Polyaluminocarbosilane As Precursor for Aluminum-Containing SiC Fiber from Oxygen-Free Sources

Preparation and characterization of near-stoichiometric silicon carbon fibres

ALUMINUM-CONTAINING SILICON CARBIDE FIBERS PREPARED FROM POLYALUMNINOCARBOSILANE AND POLYCARBOSILANE BLENDS

Preparation and Properties of Sic Fiber with A Stable Excess Carbon Layer on the Surface

Fabrication of nearly stoichiometric polycrystalline SiC fibers with excellent high‐temperature stability up to 1900°C

Preparation and Characterization of Continuous High-Temperature Resistant Si-Al-C Fibers by One-Step Method

Properties and Mechanism of High Temperature Resistance of Continuous SiC(Al) Fibers

Fabrication of Aluminum-Containing Silicon Carbide Fibers from Electrospinning