Abstract:The preparation of aluminum-containing silicon carbide,SiC(Al),fibers by using polyaluminocarbosilane(PACS) and polycarbosilane(PCS) blends as precursors was investigated.The solubility parameter of PACS was determined to be 18 MPa 1/2 by dissolving PACS in solvents with different solubility parameters.It was very close to the solubility parameter of PCS(18.4 MPa 1/2),indicating the possible compatibility of PACS and PCS.After PACS and PCS both were dissolved in xylene,a translucent yellow blend of PACS and PCS,B-PACS,was obtained by distillation.The composition and structure of B-PACS,PACS and PCS were characterized by chemical analysis,GPC and FTIR.It was found that B-PACS with desirable Al contents could be obtained by adjusting the ratio of PACS(Al content 1.25 wt%) and PCS.The Si—H bond content can be indicated by A_ 2100 cm-1 /A_ 1250 cm-1,where A_ 2100 cm-1,A_ 1250 cm-1 are the absorbance of Si—H bonds at 2100 cm-1 and CH_3 bonds at 1250 cm-1,respectively.The FTIR results showed that the Si—H bond content of B-PACS was higher than that of PACS,while their Al contents were the same.PCS with a higher Si-H content might be responsible for the higher Si—H content of B-PACS.GPC results showed that B-PACS had a high molecular weight fraction as compared with PACS of the same Al content.The apparent activation energy of flow for B-PACS and PACS(Al content 0.6 wt%) was determined by the relationship between temperature and melt viscosity.They were 200 kJ/mol and 255 kJ/mol,respectively.The better spinnability of B-PACS was approved by spinning experiments,and finer B-PACS green fibers were obtained.The tensile strength of Si-Al-C-O fibers from PACS and B-PACS were 2.0 GPa and 2.4 GPa,respectively.The higher strength of Si-Al-C-O fibers from B-PACS might be related with the finer diameter of the green fibers and the high molecular weight fraction in B-PACS.The SiC(Al) fibers derived by curing PACS and B-PACS green fibers at 1800℃ in Ar were compact and smooth,while the SiC fibers derived from PCS had pores and defects.The introduction of Al into SiC fibers may reduce the growth of SiC crystallites in fibers.The average sizes of SiC crystallites in fibers derived from B-PACS,PACS and PCS were 8.5 nm,9.6 nm and 14 nm,respectively.

ALUMINUM-CONTAINING SILICON CARBIDE FIBERS PREPARED FROM POLYALUMNINOCARBOSILANE AND POLYCARBOSILANE BLENDS

LIQUID POLYCARBOSILANE DERIVED AI-CONTAINING SiC CERAMIC PRECURSORS——POLYALUMINOCARBOSILANE

Single-source-precursor synthesis and characterization of SiAlC(O) ceramics from a hyperbranched polyaluminocarbosilane

Fabrication of SiC ultrafine fiber with low oxygen content by electrospinning, thermal curing and pyrolysis of cyano-polycarbosilane

SiAlC ceramics from a new polyaluminocarbosilane: Synthesis, structure and oxidation behaviors

Flexible and thermally stable SiC fiber mats derived from electrospun boron-doped polyaluminocarbosilane precursors

Carbon-bonded Carbon Fiber Composites Containing Uniformly Distributed Silicon Carbide

Synthesis of Polytitanocarbosilane and Preparation of Si–C–Ti–B Fibers

Synthesis of cyano-polycarbosilane and investigation of its pyrolysis process

A novel pretreatment strategy for accurate determination the Al element content within polyaluminumcarbsilane

Aqueous Processing, Hot-Pressing and Mechanical Properties of Silicon Carbide with Al2O3 and Y2O3

In situ formation of Si3N4–SiC nanocomposites through polymer-derived SiAlCN ceramics and spark plasma sintering

Boron-carbon doped Silicon Carbide Fibers: Preparation and Property

Slurry‐impregnating hot‐press sintered silicon carbide nanofiber/silicon carbide composites with Al‐B‐C as sintering additives

Elemental and structural evolution of polymer-derived SiC fibers fabricated via solution blend and iodine curing methods

Fabrication, microstructure, and properties of SiC/Al4SiC4 multiphase ceramics via an in-situ formed liquid phase sintering

Structure and properties of fine diameter continuous SiC ceramic fiber reinforced Al matrix composites

Allyl-Substituted Hydridopolycarbosilane with Low Curing Temperature and High Ceramic Yield under a Redox Initiation System

Preparation and Properties of Nano-Silica/Calcium Alginate Blend Fibers

Improving SiC grain growth and reducing carbon content in pyrolyzed polycarbosilane using nanosized Si particles

Reinforcing poly(lactic acid)/poly(butylene succinate) biodegradable blends with silicon carbide (SiC): A silane‐coupled approach for enhanced mechanical and thermal performance