Abstract:Reducing the Oxygen content in SiC fibers is important to enhance the high-temperature resistance of the fibers. For this aim, the low-molecular-weight polycarbosilane(LM-PCS) was recomposed into high-molecular-weight PCS(HM-PCS) which was then dissolved in xylene to form the spinning solutions of different concentration of the precursors. Subsequently, PCS fibers were dry spun from the solutions, and were pyrolyzed into the SiC fibers. The oxygen content in the fibers formed under a special heating procedure without air-curing was 3.41wt%. The tensile strength of the fibers retained 91% after heat treatment for 1 h in air at 1000 degrees C. The removal of the residual solvent, the self cross-linking process and the ceramization process during the fiber formation were followed by IR, XRD, SEM, gel content and TG-DTA of green PCS fibers. Four stages of reactions were involved in the pyrolysis process of PCS fibers with the increase of temperature: (1) T <250 degrees C: the volatilization of the moisture absorbed from atmosphere and the residual amounts of solvent, (2) T = 250 similar to 550 degrees C: self cross-linking between molecules, (3) T=550 similar to 750 degrees C: transformation of the polymer to ceramics and (4) T=750 similar to 1250 degrees C: transformation of the amorphous phase to crystallization. Self cross-linking was mainly the cross-linking between Si H bonds and Si-CH3 bonds in the range of 250 similar to 550 degrees C. During the self cross-linking, a small amount of oxygen from the atmosphere went into the cross-linking reaction.

Flexible and thermally stable SiC fiber mats derived from electrospun boron-doped polyaluminocarbosilane precursors

Fabrication of SiC ultrafine fiber with low oxygen content by electrospinning, thermal curing and pyrolysis of cyano-polycarbosilane

The preparation of SiC ultrafine fibers containing low amount of oxygen by the electrospinning and pyrolysis of vinyl-modified polycarbosilane

Amorphous Fine-Diameter SiC-based Fiber from a Boron-Modified Polytitanocarbosilane Precursor

Boron-carbon doped Silicon Carbide Fibers: Preparation and Property

Preparation of Polymer-Derived Boron-Containing Silicon Carbide Fibers

Flexible ultrafine nearly stoichiometric polycrystalline SiC fibers with excellent oxidation resistance and superior thermal stability up to 1900 °C

Facile Synthesis of Melt-Spinnable Polyaluminocarbosilane Using Low-Softening-point Polycarbosilane for Si–C–Al–O Fibers

Modification of polycarbosilane by polyborazine as a precursor for oxygen-free SiC fibersElectronic supplementary information (ESI) available: DSC thermograms; molecular weight distributions; chromatograms of hydrogen evolution; 29Si NMR spectra. See http://www.rsc.org/suppdata/jm/b3/b303573e/

STUDY OF HIGH TEMPERATURE RESISTANT SiC(Al) FIBERS PRECURSOR-POLYALUMINOCARBOSILANE FIBERS

Microstructure and Thermal Stability of Low-Oxygen SiC Fibers Prepared by an Economical Chemical Vapor Curing Method

Flexible Hydrophobic And Lipophilic Aluminum-Doped Silicon Carbide Fibrous Mats Synthesized By Electrospinning Polyaluminocarbosilane

Synthesis and Structural Characterization of SiBOC Ceramic Fibers Derived from Single-Source Polyborosiloxane

Modification of polycarbosilane as a precursor with high ceramic yield for oxygen-free SiC fibers

The Preparation and Properties of High Temperature Resistant Sic(Al) Fibers

Enhanced High‐temperature Resistance and Magnetic Property of SiFeC Nanocomposites Containing a Small Amount of Boron

Preparation and characterization of lightweight SiC frameworks by connecting SiC fibers with SiC joints

Preparation of Low Oxygen SiC Fiber by Dry Spinning

Silicon Carbide Base Ceramic Fiber Synthesis from Polycarbosilane-Modified Polymethylsilane Blend Polymers by Melt Spinning

Hierarchically porous SiC ultrathin fibers mat with enhanced mass transport, amphipathic property and high-temperature erosion resistance

SiC FIBERS WITH A LOW OXYGEN CONTENT PREPARED BY ELECTRON BEAM RADIATION CURING