Abstract:Polycarbosilane (PCS) serves as a crucial precursor for silicon carbide (SiC) fibers and ceramics. However, both of the precursor and the resulting SiC ceramics are carbon-rich, which is often viewed as detrimental to their relevant high-temperature properties. In this work, PCS is modified using nanosized Si particles to improve SiC grain growth and reduce carbon content in the resulting SiC ceramics, and the structural evolution during the polymer–ceramic conversion process has been meticulously investigated. The findings reveal that the incorporation of nano-Si into PCS raises its actual ceramic yield and accelerates the organic-inorganic conversion process. This is attributed to the formation of a more crosslinked structure at 200 °C–350 °C, resulting from the reaction between the Si–OH groups in nanosized Si and the Si–H and Si–CH3 groups in PCS. The carbothermic reaction between nano-Si and the free carbon starts at approximately 1200 °C at the periphery of nanosized Si particles, and is accomplished at around 1400 °C. This leads to the formation of large-sized reactive β-SiC. Simultaneously, PCS-derived β-SiC with smaller sizes is also formed at 1300 °C–1400 °C. At 1600 °C–1800 °C, the growth of the reactive and the derived β-SiC in nano-Si-modified PCS is both accelerated due to a substantial decrease in the free carbon content. Consequently, the grain size of β-SiC is much larger than that of unmodified PCS. Additionally, the residual amorphous free carbon transforms into nanocrystalline carbon at around 1400 °C and evolves into graphite carbon at 1600 °C–1800 °C, which exhibits a more ordered structure with larger size compared to that in unmodified PCS.

LIQUID POLYCARBOSILANE DERIVED AI-CONTAINING SiC CERAMIC PRECURSORS——POLYALUMINOCARBOSILANE

Single-source-precursor synthesis and characterization of SiAlC(O) ceramics from a hyperbranched polyaluminocarbosilane

SiAlC ceramics from a new polyaluminocarbosilane: Synthesis, structure and oxidation behaviors

A novel pretreatment strategy for accurate determination the Al element content within polyaluminumcarbsilane

Synthesis of cyano-polycarbosilane and investigation of its pyrolysis process

Allyl-Substituted Hydridopolycarbosilane with Low Curing Temperature and High Ceramic Yield under a Redox Initiation System

Improving SiC grain growth and reducing carbon content in pyrolyzed polycarbosilane using nanosized Si particles

Evaluation of Poly(methylsilane‐carbosilane) Synthesized from Methyl‐dichlorosilane and Chloromethyldichloromethylsilane As a Precursor for SiC

Facile synthesis of a carbon-rich SiAlCN precursor and investigation of its structural evolution during the polymer-ceramic conversion process

Preparation of SiC ceramic fiber from a photosensitive polycarbosilane

One-pot Synthesis and Characterization of Liquid Polycarbosilanes

Synthesis and Characterization of Grafted Silicone Polycarbonates

Influence of polycarbosilane composition on the properties of SiC/SiC composite fabricated by precursor infiltration and pyrolysis process

A New SiC Precursor with High Ceramic Yield: Synthesis and Characterization of CHxMeSiH2‐containing Poly(methylsilane‐carbosilane)

Fabrication, microstructure, and properties of SiC/Al4SiC4 multiphase ceramics via an in-situ formed liquid phase sintering

Properties of SiC Ceramics Sintered via Liquid Phase Using Al2O3 + Y2O3, Al2O3 + Yb2O3 and Al2O3 + Dy2O3 as Additives: a Comparative Study

The Structural Evolutions and Enhanced Thermal Stability of Al Cation-Modified Silicon Oxycarbide Ceramics

Flexible and thermally stable SiC fiber mats derived from electrospun boron-doped polyaluminocarbosilane precursors

Crystal Chemistry at Interfaces Between Liquid Al and Polar SiC{0001} Substrates

[Preparation of polyaluminum silicate chloride (PASC) from tetraethylorthosilicate (TEOS) and its physicochemical characteristics].

Fabrication of SiC ultrafine fiber with low oxygen content by electrospinning, thermal curing and pyrolysis of cyano-polycarbosilane