Abstract:SiC-MgAl2O4 composite refractories were prepared by using SiC particles, MgAl2O4 powders, α-Al2O3 micro-powders and metal Al powders as raw materials under flowing nitrogen at 1450 °C. The creep test was conducted at 1400 °C under 0.2 MPa for 50 h and the effects of Al addition on the creep resistance of SiC-MgAl2O4 composite refractories were investigated. The results show that the creep rate of samples without Al addition increases gradually as time prolonging while the samples with Al addition has a better creep resistance and the creep rate always contains a low creep rate. The mechanism for improving creep resistance of the samples with Al addition could be concluded as follow. During the creep test, the samples have a oxygen concentration from surface areas to the inner areas. (Al2OC)x-(AlN)(1-x) whiskers (generated during the sintering process) at the surface area preferentially reacts with oxygen to form Al2O3 and a little SiC oxidizes to SiO and even SiO2, the formed Al2O3 and SiO/SiO2 can react with the MgAl2O4 matrix to generate mullite, cordierite and MgO. MgO and SiO/SiO2 could also transfer and react with Al2O3 to generate new MgAl2O4 particles and even plate β-Sialon dispersed in pores where (Al2OC)x-(AlN)(1-x) whiskers ever existed. The formation of mullite, cordierite, MgAl2O4 particles and plate β-Sialon had a synergistic effect to improve the creep resistance. Besides, these new phases could fill the pores and inhibit the diffusion of oxygen inside the samples. With a relative low oxygen partial pressure inside, most of the (Al2OC)x-(AlN)(1-x) whiskers still existed in samples with a network structure and only partly oxidized to Al2O3, the oxidation of SiC was inhibited and formation of liquid was avoided. Thus, the creep resistance of the sample was further enhanced.

HIGH-TEMPERATURE RESISTANCE PROPERTIES OF SILICON CARBIDE FIBERS CONTAINING ALUMINUM

SiC fibers with different diameters exhibiting excellent high-temperature resistance and oxidation resistance

Flexible ultrafine nearly stoichiometric polycrystalline SiC fibers with excellent oxidation resistance and superior thermal stability up to 1900 °C

Effect of long-time annealing at high temperature on the microstructure and mechanical properties of different types of SiC fibers

Study on the oxidation mechanism of Al-SiC composite at elevated temperature

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

Temperature Resistance Properties of Unidirectional Laminated C f/SiC-Al Prepared by PIP and Vacuum Pressure Infiltration

Effect of Silicon Addition and Thermal History on the Thermal Expansion Behavior of Sic/Al Composites

Preparation of Continuous Aluminum Oxide Fibers with Silicon Oxide and Zirconium Oxide Additives

High-temperature resistance and thermal insulation performance of continuous SiMOC ceramic fibers fabricated by the modified sol-gel method combined with dry spinning

Mechanical Properties of Si3N4/BN Fibrous Monolithic Ceramics at Elevated-Temperature

Effect of SiC on the anti-ablation resistance and flexural strength of (Hf-Ta-Zr)C-C/C composites

Effects of SiC contents on the microstructure and mechanical properties of Al4SiC4–SiC ceramic composites

Preparation and Thermal Ablation Behavior of HfB2–SiC‐Based Ultra‐High‐Temperature Ceramics under Severe Heat Conditions

High Temperature Mechanical Property of Al2O3 Coated Quartz-Fiber Reinforced Methyl Silicon Resin Composites

High-temperature properties of Al 2 O 3 /SiO 2 composites

Preparation and high-temperature properties of skin–core structure SiC ceramic fibers

High-temperature Deformation Behavior of SiC-AlN Ceramic Alloys with Fine-grained Microstructure.

Creep behaviour of an Al–Si–Al2O3 composite based on phase evolution at 1300oC

Effect of Al addition on creep resistance of the fired SiC-MgAl2O4 composite refractories

Structure and properties of fine diameter continuous SiC ceramic fiber reinforced Al matrix composites