Abstract:Polyvinyl chloride (PVC) is the most widely used general flame-retardant plastic worldwide; however, the large number of plasticizers added during processing significantly reduces its flame-retardant property. To prepare a new type of PVC material with highly efficient flame retardancy and smoke suppression, antimony trioxide (Sb2O3), talc powder, hydromagnesite, and zinc borate were added in different proportions to PVC to explore the flame-retardant properties, thermal weight, smoke density (Ds), and mechanical properties of the composite materials. Results showed that the limiting oxygen index value of each group was higher than 27% after adding talc powder, magnesite, and zinc borate to replace part of the Sb2O3. This value was within the refractory-grade level and indicated a good flame retardancy performance. The replacement effect was in line with the experimental expectation. The lowest Ds peak value was 656.4 when the flame retardants were added with 10 wt% Sb2O3, 50 wt% hydromagnesite, 20 wt% talc, and 20 wt% Zn3BO6. Compared with pure Sb2O3 as a flame retardant, the Ds peak value decreased by 46.7%. The thermogravimetric decomposition temperature of the composites in each group was generally higher than that of the group with pure Sb2O3 as a flame retardant, increasing by 45.3 °C. The thermal stability of the composites was improved, and the elongation at the break and tensile strength were 234.9% and 25.8 MPa, respectively, indicating good mechanical properties. The results showed that using compound flame retardants to replace most of the Sb2O3 is an effective technique for obtaining good flame retardancy and mechanical properties of PVC. This study, not only reduced the manufacturing cost of flame-retardant PVC, but also effectively reduced its smoke density and the time to reach the highest smoke density, which provided a research reference for the application and promotion of flame-retardant PVC.

A STUDY ON MECHANOCHEMICAL MODIFICATION OF PVC/FLAMERETARDANT AND SMOKE-SUPPRESSANT ADDITIVES SYSTEM

Study on Controlled Synthesis of Zinc Carbonate Via Mixed Template and Hydroxystannate-coated Calcium Its Flame Retardancy in PVC

Biomimetic Synthesis of Zinc Hydroxystannate-Coated Calcium Carbonate and Its Application in PVC

Progress in studies on flame retardant and smoke suppressant for PVC

Improving the flame retardancy and mechanical properties of high-density polyethylene-g-maleic anhydride with a novel organic metal phosphonate

Improving the flame retardancy and smoke suppression of flexible PVC by incorporating zinc borate‐modified diantimony trioxide

Research Progress in the Fire Retardation and Smoke Inhibition of PVC

The Flame Retardancy and Smoke Suppression Performance of Polyvinyl Chloride Composites with an Efficient Flame Retardant System

Research on Fire-Retardant and Smoke-Inhibition PVC-U Formula

The Progress on the Study of Hydrotalcite-Modified PVC

Simultaneously enhanced flame retardancy and smoke suppression properties of flexible polyvinyl chloride with the incorporation of modified Mg(OH) 2 and Sb 2 O 3

Synergistic effects of inorganic tin compounds and Sb 2O 3 on thermal properties and flame retardancy of flexible poly(vinyl chloride)

Modification of ABS/PVC Blend

Thermal Stability, Smoke Emission and Mechanical Properties of Poly(vinyl Chloride)/hydrotalcite Nanocomposites

Study on the fusion properties of extruded foaming rigid PVC

Bio-based Phytic Acid and Tannic Acid Chelate-Mediated Interfacial Assembly of Mg(OH)2 for Simultaneously Improved Flame Retardancy, Smoke Suppression and Mechanical Properties of PVC

RETRACTED ARTICLE: Preparation of Multilayers Zinc Hydroxystannate Microcapsules and its Application in Flame-Retardant PVC Composites

Low-melting sulfate glasses as additives to semirigid PVC and their flame retardant and smoke suppressant properties

Enhanced flame retardancy and thermal stability of zinc borate and magnesium carbonate as a promising alternative for Sb2O3 toward polyvinyl chloride

Flame Retardancy and Smoke Suppression of Molybdenum Trioxide Doped Magnesium Hydrate in Flexible Polyvinyl Chloride

Surface Modification of Super-Fine Magnesium Hydroxide Powder and It’s Flame-Retardant Treatment of Flexible PVC