Study on Controlled Synthesis of Zinc Carbonate Via Mixed Template and Hydroxystannate-coated Calcium Its Flame Retardancy in PVC

徐建中,彭飞,焦运红,王宁
DOI: https://doi.org/10.19491/j.issn.1001-9278.2011.11.017
2011-01-01
Abstract:Using sodium dodecyl benzene sulfonate (SDBS) as a template in the mixed solution of glycol and water, zinc hydroxystannate-coated calcium carbonate (ZHSCC-1) was prepared. Zinc hydroxystannate-coated calcium carbonate (ZHSCC-2) was prepared in an aqueous solution without SDBS/glycol for comparison. Both ZHSCC-1 and ZHSCC-2 were studied as the flame retardant of PVC. XRD, SEM, and TG-DSC showed that zinc stannate was coated on CaCO3 surface and the product was thin hexagonal pieces with the size about 5 um. At the same loading, not only the flame retardancy and smoke suppressant effects, but also the tensile strength, elongation at break, and impact strength of ZHSCC-1 flame retarded PVC were better than those of ZHSCC-2 flame retarded system.