Organic-Inorganic Hybrid Film Modified with Silica and Alumina Sols by Sol-Gel Method
Lu Jingjuan,Guo Xingzhong,Yang Hui
DOI: https://doi.org/10.3321/j.issn:1002-185X.2008.z2.030
2008-01-01
Rare Metal Materials and Engineering
Abstract:With the polycondensates of methyltrimethoxysilane (MTMS) as film forming materials, the alumina sols prepared by aluminium isopropoxide and silica sols prepared by tetraethylorthosilicate (TEOS) as inorganic reinforcing materials, 3-(methacryloxypropyl)-trimethoxysilane (KH-570) as surface modifier, the organic-inorganic film was prepared on polycarbonate (PC) by co-condensation reaction. The properties of coating solution and film were studied by ubbelohde viscosity test, TG/DTA, FTIR, UV-Vis, metallographic microscope, pencil hardness and cross-cut test. The results show that the addition of KE-570 improves the stable property of the coating solution. The cross-linked inorganic structure endcapped with organic groups forms on the PC by the co-condensation reaction between hydrolysis products of MTMS, TEOS and aluminium isopropoxide, whose base backbone is composed of Si-O-Si, Si-O-Al, Al-O-Al network structure. The heat-resistance and hardness of the film increase with the addition of alumina sols. The organic-inorganic film improves the transparency of PC and the addition of KH-570 has better effect on the transparency when coating solution is aged for 2 d before coating. The surface of the film becomes smooth and homogeneous after the addition of KH-570.