Abstract:SiC layer was prepared in an industrial scale spout fluidized bed by chemical vapor deposition. The density of SiC coating was about 3.18 g/cm(3). High temperature oxidation experiments were carried out at different temperatures from 800 to 1600 degrees C. The microstructure and composition were characterized using different methods, including mass change weighing, XRD, EDS and SEM. It was found that the weight gain of SiC coating layer was not obvious below 1200 degrees C, and subsequent mass gain gradually increased with increasing temperature, reaching 10% at 1600 degrees C. High-magnification SEM results show that the oxidation began from the surface and gradually formed punctate distribution of the oxide. Small crystal structure (similar to micron) of the SiC surface was very clear at 1000 degrees C, and this crystal structure disappeared gradually at high temperatures, forming oxides of Si in the SiC surface. There was a stacking fault stress due to the different thermal expansion coefficients and elastic modulus of SiC and Si oxides, leading to the gradual formation of cracks around the punctates. With increasing temperature, the crack further increased the oxidation rate of SiC, and finally the formed Si oxides layer fell off from the particles. It can be seen clearly that the layer was peeling when the temperature was increased to 1400 degrees C. Increasing the temperature to 1600 degrees C, the SiC coating was oxidized completely into a honeycomb structure, with obvious sintering of SiC. XRD analysis shows that there was a growing SiO2 peaks from 1400 degrees C, indicating that surface oxidation was significant. EDS results shows that the oxygen content in the coating surface gradually increased with increasing temperature. Semi-quantitative analysis shows that the surface was close to SiO2 at 1600 degrees C.

PREPARATION OF SiC COATING BY CHEMICAL VAPOR REACTION

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Study on the High Speed Chemical Vapor Deposition for SiC Coating

Preparation, Performance and Nuclear Applications of Silicon Carbide Materials Prepared by FB-CVD Method

Interfacial modification and oxidation resistance behavior of a CVD-SiC coating for C/SiC composites

Silicon Carbide Composites Deposited in Silicon Carbide Whiskers by Cvi Process

Oxidation resistance improvement of carbon fiber nonwoven fabrics through SiC coating technology

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Siliconization elimination for SiC coated C/C composites by a pyrolytic carbon coating and the consequent improvement of the mechanical property and oxidation resistances

High Temperature Oxidation Behavior of SiC Coating Materials

Effect of Si, Al2O3 additives on the ablation behavior of ZrB2-SiC coating with Al2O3-modified SiC bond coat for C/C composites

SiC Coatings Fabricated by Chemical Vapor Reaction on Graphite

Investigation of Impact of C/Si Ratio on the Friction and Wear Behavior of Si/SiC Coatings Prepared on C/C-SiC Composites by Slurry Reaction Sintering and Chemical Vapor Infiltration

Effect of Al2O3 addition on the microstructure and oxidation behavior of SiC coating prepared by pack cementation on C/C composites

Interfacial Reactions and Mechanical Properties Studies of C-Coated and C/B4C Duplex-Coated SiC Fiber-Reinforced Ti2AlNb Composites

In-situ SiC nanowires reinforced SiC-based multicomponent ceramic coating for protecting SiOC/CF composites

An oxidation protective coating prepared by SiC densifying HfB2-SiC skeleton for SiC-coated C/C composites at 1473, 1773, and 1973 K

Comparison of Oxidation Behaviors of 3D C/PyC/SiC and SiC/PyC/SiC Composites in an O2-Ar Atmosphere

Characteristics of ZrC Barrier Coating on SiC-Coated Carbon/Carbon Composite Developed by Thermal Spray Process

A gradient composite coating to protect SiC-coated C/C composites against oxidation at mid and high temperature for long-life service