A Study of Oxidation Protection Coatings of Cf/SiC Composite

邹世钦,张长瑞,周新贵,曹英斌,周长城

DOI: https://doi.org/10.3969/j.issn.1001-2486.2004.04.012

2004-01-01

Abstract:The hindrance which currently precludes the use of Cf/SiC composites is the oxidation of carbon fiber at the temperature higher than 400°C. Therefore, it is necessary to develop coatings capable of protecting Cf/SiC components from oxidation. These coatings consist of three layers, a CVD-SiC bonding layer, a self-sealing active layer by forming glassy phases on exposure to oxygen, and a CVD-SiC erosion resistant layer. Oxidation test was carried out. The results indicated that the samples with only CVD-SiC coating have much mass loss, and the samples with three layers of coatings including a self-sealing active layer have little mass loss from the temperature of 800°C to 1200°C. Samples with self-sealing active layer which underwent an oxidation test at 1000°C in the atmosphere for 288 hr suffered only 2.3% mass loss and a residual strength of 452.9 MPa. At the same time, CVD-SiC shows various appearance after oxidation at 800°C, 1000°C, and 1200°C. The surface formed at 1200°C has some liquid phase characteristics.